Paper Titles
Effect of Laser Scanning and Aging Treatment on Microstructure and Property of Austenitic Heat-Resistant Steel
p.416
Argon-Oxygen Post-Discharge Treatment of Hexatriacontane: Heat Transfer between Gas Phase and Sample
p.421
Multiple Needle Cathodes Plasma Surface Alloying of Ti6Al4V with W-Mo-C-N
p.426
Influence of Oxygen Plasma Treatment on Surface Properties of Armos Fiber
p.430
Preparation of Epoxy Modified Organosilicone High-Temperature Resistance Coatings
p.434
Research on Friction and Wear Performance of Brake Disc Pair Materials for New Type of Drilling Rig
p.438
Influence of the Plating Conditions on the Structure and Corrosion Resistance of the Ni-Mn Alloy
p.442
Microstructural Evaluation of High Oxidation Resistant CrAlSiN Hard Coating at Elevated Temperature in Air Atmosphere
p.446
Study on the Characteristics of Wear Resistance Using Silicate Particles as Additive on the Metal Friction Pairs
p.452

Preparation of Epoxy Modified Organosilicone High-Temperature Resistance Coatings

Article Preview

Abstract:

An ambient-cured organosilicone resin modified with epoxy resin was synthesized with lab-synthesized polysiloxane resin and biphenix-A epoxy resin(E-20) by copolymerization at 180~190 °C for 2~3 hours. The effect of ratios between polysiloxane resin and E-20, reaction temperatures and reaction time on heat resistance and miscibility etc were discussed in detail. The experiment results showed that the epoxy modified organosilicone resin exhibited the best solubility performance and adhesion strength when the ratio of the polysiloxane resin to E-20 was 3:7. The Fourier transform infrared spectra (FTIR) revealed that hydroxy on epoxy resin had reacted with ethyoxyl on organic silicon molecular chain, but no ring-opening reaction happened on epoxy group of E-20. The excellent high-temperature resistance painting, based on these epoxy modified organosilicone resin was prepared with flake aluminum powder as temperature resistance filler, polyamide 650 as curer and WD-50 coupling agent as curing-promoter. It was shown that the temperature resistance was superior to 600°C and the adhesion strength of the coating was up to 1 grade. Scanning electron microscope(SEM) revealed the reaction happened on -Si-O-Si- and Al under high temperature improved the coatings to resist higher temperature. The mechanism of the high-temperature anticorrosion is attributed to “ring-opening reaction” and “cross-link solidification reaction”.

You might also be interested in these eBooks
Surface Engineering View Preview

Info:

Periodical:

Key Engineering Materials (Volumes 373-374)

Pages:

434-437

DOI:

https://doi.org/10.4028/www.scientific.net/KEM.373-374.434

Citation:

Cite this paper

Online since:

March 2008

Authors:

Hua Zhu, Zhi Lang Chen, Fang Nan, An Lin, Fu Xing Gan

Keywords:

Epoxy Modified Organosilicone Resin, Flake Al Powder, High-Temperature Resistance Coatings

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

© 2008 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

References

[1] Mathivanan L, Radhakrishna S. Heat-resistant anti-corrosive paint from epoxy-silicone vehicles, Anti-Corrosion Methods and Materials, vol. 44 (1997), p.400.

DOI: 10.1108/00035599710185476

Google Scholar

[2] Liu Guangj uan, Zuo Yu, Zhao Jingmao, Heat Resistance and Corrosion Resistance of Epoxy-silicone based coating, Corrosion and Protection, vol. 25 (2004), p.238.

Google Scholar

[3] James Franklin Hyde, Midland Mich, Room Temperature Curing Organopoly - Silicone Resins. US. Patent 3, 350, 349(1967).

Google Scholar

[4] Zhang Wenjuan, Chen Jianhua. The organosilicone coating with high temperature resistance and its adhesive, Organosilicone material, vol. 16(2002).

Google Scholar