Mechanical and Thermal Properties of Ultra-High Carbon Steel Containing Aluminum

Article Preview

Abstract:

The properties of ultrahigh carbon steels (UHCS) are strongly influenced by aluminum additions. Hardness studies of quenched UHCS-Al alloys reveal that the temperature for the start of transformation increases with increases in aluminum content. It is shown that this change is a function of the atomic percent of solute and of the valence state when comparisons are made with UHCSs containing silicon and tin as solutes. The thermal expansion of UHCSs with dilute aluminum additions shows no discontinuity in the vicinity of the ferrite-austenite transformation temperature. This is the result of a three phase region of ferrite, carbides and austenite. The slope of the expansion curve is higher in the austenite range than in the ferrite range as a result of the dissolution of carbon in austenite with temperature. Processing to achieve a fine grain size in UHCS-Al alloys was principally by hot and warm working (HWW) followed by isothermal warm working (IWW). The high temperature mechanical properties of a UHCS-10Al-1.5C material show nearly Newtonian-viscous behavior at 900 to 10000C. Tensile elongations of 1200% without failure were achieved in the 1.5%C material. The high oxidation corrosion resistance of the UHCS-10Al materials is described.

You might also be interested in these eBooks

Info:

Periodical:

Materials Science Forum (Volumes 539-543)

Pages:

4844-4849

Citation:

Online since:

March 2007

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2007 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

[1] O.D. Sherby, B. Walser, C.M. Young and E.M. Cady: Scripta Met. Vol. 9 (1975), p.569.

Google Scholar

[2] O.D. Sherby and J. Wadsworth: Encyclopedia of Materials and Engineering (Pergamon Press 1988), Supplementary Volume 1, p.519 and 541.

Google Scholar

[3] D.R. Lesuer, C.K. Syn, A. Goldberg, J. Wadsworth and O.D. Sherby: J. Metals (JOM) Vol. 45 (1993), p.40.

DOI: 10.1007/bf03222405

Google Scholar

[4] J. Wadsworth: Deformation, Processing and Properties of Structural Materials (E.M. Taleff, C.K. Syn and D.R. Lesuer, Eds. TMS, Warrendale, PA, 2000), p.3.

Google Scholar

[5] O.D. Sherby, O.A. Ruano, M. Carsi, and T. Oyama: The Johannes Weertman Symposium (R.J. Aresenault et al. Eds, TMS, Warrendale, PA, 1996), p.3.

Google Scholar

[6] M. Carsi, A. Fernandez-Vicente, O.A. Ruano and O.D. Sherby: Mats. Sci. & Technol. Vol. 15 (1999), p.1087.

Google Scholar

[7] C.K. Syn, D.R. Lesuer and O.D. Sherby: Met. Trans. A Vol. 25A (1994). P. 1481.

Google Scholar

[8] H. Fukuyo, H.C. Tsai, T. Oyama and O.D. Sherby: ISIJ Int'l. Vol. 31 (1991), p.76.

Google Scholar

[9] H.C. Tsai: Superplasticity in Ultrahigh Carbon Steels and Their Laminates (Ph.D. Thesis, June 1990, Stanford University, Stanford, CA).

Google Scholar

[10] H. Fukuyo: Influence of aluminum, tin and silicon on the superplastic behavior of ultrahigh carbon steel (Engineer Thesis, June 1987, Stanford University, Stanford, CA).

Google Scholar

[11] O.A. Ruano, T. Oyama and O.D. Sherby: Proceedings, Thermec 2006 conference.

Google Scholar

[12] J. Wittenauer, P. Schepp and B. Walser: Superplasticity and Superplastic Forming (C.H. Hamilton and N.E. Paton, Eds, TMS, Warrendale, PA, 1988), p.507.

Google Scholar

[13] J. Wadsworth and O.D. Sherby: Thermomechanical Processing and Mechanical Properties of Hypereutectoid Steels and Cast Irons (D.R. Lesuer, C.K. Syn and O.D. Sherby, Eds. TMS, Warrendale, PA, 1997), p.1.

Google Scholar