Surface Modification of Li (Co1/3Mn1/3Ni1/ 3)O2 Fine Powders Using Aqueous Al2O3 Sol

Seon Hye Kim; Kwang Bo Shim; Kyoung Ran Han; Chang Sam Kim

doi:10.4028/www.scientific.net/MSF.544-545.857

Paper Titles

Study on Silver-Containing HA Coatings Prepared by Vacuum Plasma Spraying
p.841

Study on the Precise Alignment of Micro-Lenses in the Microcolumn by Using the Laser Diffraction Pattern
p.845

A Study on Vacuum Plasma Spraying Tungsten Coatings
p.849

Supercritical Impregnation of Organic Phase Change Materials into Polyester Fiber
p.853

Surface Modification of Li (Co_1/3Mn_1/3Ni_{1/ 3})O₂ Fine Powders Using Aqueous Al₂O₃ Sol
p.857

Synthesis and Characterization of Ag-Pd Nanoparticles by a Reverse Micelle Process
p.861

Synthesis and Characterization of CoFe₂O₄ Nanoparticles by Glycothermal Process
p.865

Synthesis and Characterization of Nano-Size CoAl₂O₄ Spinel Powder Using Sol-Gel Process
p.869

Synthesis and Characterization of Sr_1-xLa_xFe_12-yCo_yO₁₉ Nanoparticles Prepared by a Sol-Gel Method Using Propylene Oxide
p.873

HomeMaterials Science ForumMaterials Science Forum Vols. 544-545Surface Modification of Li (Co1/3Mn1/3Ni1/ 3)O2...

Surface Modification of Li (Co_1/3Mn_1/3Ni_{1/ 3})O₂ Fine Powders Using Aqueous Al₂O₃ Sol

Abstract:

The surface of Li(Ni1/3Co1/3Mn1/3)O2 was modified with Al2O3 using aqueous alumina sol and the electrochemical properties of the coated oxide were measured and compared with both uncoated and Al-doped one. The alumina coated powder showed 185 mAh/g at first cycle, and 139 mAh/g after 50 cycles in the voltage range of 3.0~4.6 V at 1C rate. The initial discharge capacity of the coated powder was slightly lower than that of the alumina doped one, but the cycle stability of the coated was better than that of the doped.