Study of the Preparation Technology and Properties of BaBi4Ti4O15 Ceramics

Jin Liang Huang; Li Hua Li; Ke Zhang; Biao Yin

doi:10.4028/www.scientific.net/MSF.561-565.499

Paper Titles

Phase Equilibria and Atomic Diffusion in the Ir/CoAl System
p.477

Microstructures and Mechanical Properties of Ti-48Al-2Cr-2Nb-xW
p.481

Improvement of Strength, Weibull Modulus and Damage Tolerance of SiC
p.489

Hydrothermal Synthesis of Bi_1.5ZnNb_1.5O₇ Nanopowders
p.495

Study of the Preparation Technology and Properties of BaBi₄Ti₄O₁₅ Ceramics
p.499

Edge Effects in Sliding Wear Behavior of ZrO₂-WC Composites and WC-Co Cemented Carbides
p.503

Study of Water-Debinding for Ceramic Parts by Injection Molding
p.507

Millimeter-Wave Assisted Sintering of Polycrystalline Yttria for Laser Host Material
p.511

Barium Titanate Nanopowders Prepared from the Modified Oxalate Co-Precipitation Method
p.515

HomeMaterials Science ForumMaterials Science Forum Vols. 561-565Study of the Preparation Technology and Properties...

Study of the Preparation Technology and Properties of BaBi₄Ti₄O₁₅ Ceramics

Abstract:

BaBi4Ti4O15 ceramics was prepared by molten salt synthesis method (MSS) and conventional solid phase process (CS). The phase of reaction products and the microstructure were detected by X-ray diffraction (XRD) and scanning electron microscope (SEM). The results show that the evident anisotropic flake structure of BaBi4Ti4O15 powder prepared by MSS was obtained at 850°C and the level of anisotropy of BaBi4Ti4O15 powder decreased with increasing temperature. After calcined at 950°C, sintering in the range of 1100~1170°C, the sintering temperature and the maximum permittivity of BaBi4Ti4O15 ceramics prepared by MSS at same frequency was lower than those prepared by CS. Additionally, the apparent degree of orientation was obtained and the lotgering factor (f) calculated according to the XRD results showed a value of 0.63.