Effects of Deformation Temperature on Dynamic Recrystallization of 7A04-T6 Alloy
  Abstract

The influences of deformation temperature on microstructure dynamic recrystallization of 7A04-T6 ultra-high strength aluminium alloy by isothermal compression experiments in different deformation temperature on the 6300KN extrusion press. The experimental results show that both tensile strength and elongation increased with deformation temperature increasing. At 480°C, tensile strength reached 582Mpa and elongation increase to 9%. In the experiment, dynamic recrystallization of 7A04 aluminium alloy is mainly grain boundary nucleation and second phase particle nucleation. The grain size of 7A04-T6 aluminium alloy gradually refined with the deformation temperature increasing. Fracture morphology showed that rupture is belong to mixed rupture of intergranular and transgranular. With the deformation temperature increase to 480°C, grain size become small, the dimple in the fracture increase gradually, and existing the second phase particle in the dimple.

  Info
Periodical
Chapter
Chapter 1: Materials Science and Engineering
Edited by
Dongye Sun, Wen-Pei Sung and Ran Chen
Pages
121-125
DOI
10.4028/www.scientific.net/AMM.121-126.121
Citation
J. M. Yu, Z. M. Zhang, Q. Wang, B. H. Zhang, "Effects of Deformation Temperature on Dynamic Recrystallization of 7A04-T6 Alloy", Applied Mechanics and Materials, Vols. 121-126, pp. 121-125, 2012
Online since
October 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Chang Liang Li, Hua Ding, Yong Qing Zhao, Lian Zhou
Abstract:Superplastic forming provides a good way for Ti alloys which are usually difficult to be deformed. Ti75 alloy with a nominal composition of...
2969
Authors: Zhi Min Zhang, Qiang Wang, B.C. Li, X. Zhang
Abstract:Warm compression tests of AZ31 Mg alloy were carried out at five temperatures in 30°C intervals from 210°C to 330°C. The samples of...
1813
Authors: Yong Xue, Zhi Min Zhang, Li Hui Lang, Li Li
Abstract:In the present paper a research has been made on the effect of aging on the microstructure and mechanical properties of AZ80 and ZK60 wrought...
560
Authors: Xiao Ping Luo, Lan Ting Xia, Ming Gang Zhang
Abstract:The effect of Cd and Sb addition on the microstructural and mechanical properties of as-cast AZ31 alloys was investigated and compared. The...
197
Authors: De Liang Zhang, Hong Bao Yu, Yuong Chen
Abstract:Bulk nanostructured (grain sizes in the range of 50-200nm) and ultrafine structured (grain sizes in the range of 100-500nm) -TiAl based...
149