Evolution of Micro-Orientations on Non-Oriented Silicon Steels during the Annealing Process Based on the CSP
  Abstract

In this paper, studied was the low carbon and low silicon (0.003%C,0.3%Si) cold-rolling steel sheet whose reduction ratio was 81% annealed at 870 °C in the laboratory salt-bath furnace and heated for 180s.The evolution of micro-orientations of grain coarsening at 1050°C and 1150°C on cold-rolling samples that were annealed at temperature 870°C and heated for 180s was studied by EBSD technology.

  Info
Periodical
Chapter
Chapter 1: Materials Science and Engineering
Edited by
Dongye Sun, Wen-Pei Sung and Ran Chen
Pages
137-141
DOI
10.4028/www.scientific.net/AMM.121-126.137
Citation
Z. L. Jin, W. Li, L. Z. Guo, "Evolution of Micro-Orientations on Non-Oriented Silicon Steels during the Annealing Process Based on the CSP", Applied Mechanics and Materials, Vols. 121-126, pp. 137-141, 2012
Online since
October 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: T. He, Y.D. Liu, Yan Wu, Q.W. Jiang, Gang Wang, Yan Dong Wang, Liang Zuo
Abstract:An experimental setup was designed to study the recrystallization kinetics of Interstitial Free (IF) steel in this work. The 80% cold rolled...
417
Authors: Zhi Gang Wang, Zheng Zhi Zhao, Ai Min Zhao, Jie Yun Ye
Chapter 2: Manufacturing and Design Science
Abstract:Deep drawing dual phase steel was designed and trial-produced in the laboratory. The microstructure and recrystallization texture was studied...
1223
Authors: Jie Yun Ye, Zheng Zhi Zhao, Zhi Gang Wang, Ai Min Zhao, Jing Jing Chen
Chapter 3: Iron and Steel
Abstract:C-Mn-Cr-Mo dual phase steel was piloted in laboratory. OM, SEM, tensile tests and XRD were used to characterize the microstructures,...
670
Authors: Ho Jun Bang, Ha Guk Jeong, Jong Beom Lee
B. Eco-Materials Processing and Design, Multifunctional Materials
Abstract:Mg alloy sheets exhibit the yield strength of 280 MPa and elongation of 18 % by rolling at 423 K. Elongation of Mg alloy sheets was improved...
190
Authors: Masataka Yoshino, Chikara Kami
Chapter 2: Contributed Papers
Abstract:Grain refinement is attracting attention as a strengthening method which does not depend on the alloying elements added to steels. Many...
2228