Bonding Quality of Wood-FRP Interface with Ambient Curable Epoxy Adhesives
  Abstract

Effects of glue spread, adhesive kind and curing agent ratio on bonding quality of wood-FRP (Fiber Reinforced Plastic) interface were investigated to choose the optimal adhesive and condition of bonding wood-FRP composites. Two different kinds of epoxy resin and one kind of curing agent were used to bond wood-wood and wood-FRP samples with three different glue spread. Shear strength of samples were measured by compression shear test. The results indicated that bonding strength of wood-FRP sample with glue spread of 300 g/mm2 and curing agent ratio of 40% were the best, when using the same epoxy resin and curing agent. The shear strengths of wood-FRP samples were less than those of samples without FRP. The bonding qualities of samples with E-44 epoxy resin/T-31 curing agent system were better than those of E-51 epoxy resin/T-31 curing agent system.

  Info
Periodical
Advanced Materials Research (Volumes 129-131)
Edited by
Xie Yi and Li Mi
Pages
572-575
DOI
10.4028/www.scientific.net/AMR.129-131.572
Citation
F. C. Cheng, Y. C. Hu, "Bonding Quality of Wood-FRP Interface with Ambient Curable Epoxy Adhesives", Advanced Materials Research, Vols. 129-131, pp. 572-575, 2010
Online since
August 2010
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Jun Deng
Abstract:One of the greatest drawbacks to predicting the behaviour of bonded joints has been the lack of reliable data on the mechanical properties of...
814
Authors: Dong Bin Fan, Te Fu Qin, Fu Xiang Chu
Abstract:The oil-tea cake, as the major byproduct of tea oil production, was used with phenol-formaldehyde (PF) resin to prepare a mixed interior...
2183
Authors: Yan Qin, Jin Rong Jia, Zhi Xiong Huang
Polymer Materials
Abstract:A new two-component polyurethane adhesive was prepared with castor oil used as main agent and castor oil modified TDI used as curing...
1128
Authors: Bao Wen Zhang, Jian Ping Lin, Zhi Guo Lu
Abstract:In the weld-through technique of weld-bonding process, adhesive usually suffers extremely high temperature, causing damage to adhesive and...
128
Authors: Jian Guang Zhang, Xiao Dong He
Chapter 13: Surface Engineering/Coatings
Abstract:Joining behavior of long glass fiber reinforced polypropylene (LFT) by three types of adhesive was investigated. Single-lap shear testing was...
1942