Study on Microstructure and Properties of BTBY Piezoelectric Ceramics with High Curie Temperature
  Abstract

(1-x)(0.6BIT-0.4BT)-xBiYbO3(BTBY) ceramics with high Curie temperature were prepared by the conventional processing. The effect of BiYbO3 content on the microstructure and electrical properties was investigated. The results show that the main phase of BTBY ceramics is BIT-BT, and a new phase BaBi4Ti4O15 (BBT) appeared. The grain morphology of BTPY ceramics are platelike and the grain size was significantly increased with increasing content of BiYbO3 .Tc of all the BTBY samples are above 440 . The BTBY ceramics show obvious dielectric relaxor characteristic. The dispersion factor γ, the dielectric constant εr, and the dielectric loss tanδ decreased with increasing the content of BiYbO3. When the content of BiYbO3 is 0.06, the optimal properties of BTBY ceramics are obtained, Tc is 457 , εr is 165, tanδ is 0.0223 and d33 is 10 pC·N-1.

  Info
Periodical
Advanced Materials Research (Volumes 156-157)
Edited by
Jingtao Han, Zhengyi Jiang and Sihai Jiao
Pages
1541-1544
DOI
10.4028/www.scientific.net/AMR.156-157.1541
Citation
B. Li, F. Gao, L. L. Liu, B. Xu, "Study on Microstructure and Properties of BTBY Piezoelectric Ceramics with High Curie Temperature", Advanced Materials Research, Vols. 156-157, pp. 1541-1544, 2011
Online since
October 2010
Export
Price
$35.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Hiroaki Takeda, C. Fujioka, Soichiro Okamura, Tadashi Shiosaki
1169
Authors: Zhi Wu Chen, Zhen Ya Lu
Abstract:A lead-free piezoelectric ceramic ternary system based on (Bi0.5Na0.5)TiO3 (BNT)-(Bi0.5 K0.5)TiO3(BKT)-BaTiO3(BT) near the morphotropic...
54
Authors: Qiang Chen, De Jun Lan, Yi Chen, Du Min Lin, Xi Yue, Ding Quan Xiao, Jian Guo Zhu
Abstract:Lead-free piezoelectric ceramics lithium sodium potassium niobate (LixNayK1-x-y)NbO3 (LNKN100x/100y) have been synthesized by a conventional...
199
Authors: Guang Hui Li, Zhang Lian Hong, Li Xia Peng, Min Quan Wang
Abstract:XRD, SEM, bulk density and dielectric properties measurements were used to investigate the effect of TiO2 nanopowder substitution for...
228
Authors: Chun Hong Mu, Ying Li Liu, Yuan Qiang Song, Huai Wu Zhang, Peng Liu
Abstract:CaCu3Ti4O12 presents colossal dielectric permittivity within a large temperature and frequency range, which...
321