Paper Title:
Research on the Adhesion of Stainless Steel Film on Gd by Magnetron Sputtering
  Abstract

In order to research the adhesion of sputtering protective coating of Gd. Gd substrates was coated with 1Cr18Ni9Ti by means of DC magnetron sputtering technology. The characteristics of the film were investigated by scanning electron microscopy (SEM), EDS, SPM and the adhesions of film was tested by tension test. The results show that the films of 1Cr18Ni9Ti are distributed by means of islands when the sputtering was initiated and the grains are like thin fiber. After a few minutes, the films are smooth and perfect, the interferences between 1Cr18Ni9Ti and Gd join together strongly, and the largest strength of adhesion is 24.7MPa when the sputtering density is 966 w/cm2 and the sputtering time is 8 minutes.

  Info
Periodical
Advanced Materials Research (Volumes 189-193)
Edited by
Zhengyi Jiang, Shanqing Li, Jianmin Zeng, Xiaoping Liao and Daoguo Yang
Pages
129-136
DOI
10.4028/www.scientific.net/AMR.189-193.129
Citation
X. Q. Zheng, S. K. Xie, R. X. Yi, "Research on the Adhesion of Stainless Steel Film on Gd by Magnetron Sputtering", Advanced Materials Research, Vols. 189-193, pp. 129-136, 2011
Online since
February 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Wen Zhuang Lu, Dun Wen Zuo, Min Wang, Feng Xu
Abstract:Electroplated Cr, Ni and Cu were used as interlayer for chemical vapor deposition (CVD) diamond coating on WC–Co cemented carbide cutting...
92
Authors: Ri Sheng Du, Ji Hua Peng, Xian Wen Liang, Jun Tian
Abstract:In this paper, the TiN/TiAlN duplex coatings were deposited on SKH51 tool steel by means of multi-arc ion plating. By means of SEM, Vickers...
402
Authors: Wei Bo Huang, Ping Lu, Jing Zhang, Xin Mao Li
Abstract:Coating protection becomes the primary and available method for the protection of marine concrete. Aliphatic polyurea is a new genre of...
1010
Authors: Zhao Jun Deng, Jing Liu, Zhi Hong Lu, Hui Wang, Cheng Jiang Lin
Chapter 2: Metal Casting Processes and Equipment
Abstract:The morphology of inhibition layer and adhesion of Zn coating about a 600MPa grade high Al dual phase steel were studied by grow discharge...
1669
Authors: Xiao Feng Zheng, Qi Yong Zeng, Zhu Li, Li Zheng Jiang, Feng Chen
Chapter 3: Material Engineering and Science
Abstract:By the method of orthogonal experiment, with different sputtering power, sputtering pressure, sputtering time and substrate bias, 9 NiCr-NiSi...
3748