Corrosion Behavior Research of Fe3Al Intermetallic Compound in H2S/CO2 Environment
  Abstract

The corrosion behavior of Fe3Al was studied by high temperature autoclaves in H2S/CO2 environment. By Stereo Microscope, we found that the corrosion film of Fe3Al is thin and crack at 60°C, 4.0 Mpa,after 72h in autoclaves; Phase analysis by XRD showed that the main composition of corroded products is FeS; its corrosion are Ⅲ corrosion resistant type and corrosion rating of 4, mainly pitting, and average corrosion rate of 0.2106 mm/a.

  Info
Periodical
Advanced Materials Research (Volumes 189-193)
Edited by
Zhengyi Jiang, Shanqing Li, Jianmin Zeng, Xiaoping Liao and Daoguo Yang
Pages
965-968
DOI
10.4028/www.scientific.net/AMR.189-193.965
Citation
B. Wang, J. H. Bai, D. M. Zhou, Z. Y. Jiang, Z. Yang, J. L. Zhang, "Corrosion Behavior Research of Fe3Al Intermetallic Compound in H2S/CO2 Environment", Advanced Materials Research, Vols. 189-193, pp. 965-968, 2011
Online since
February 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Weon Ju Kim, Seok Min Kang, Ji Yeon Park
Abstract:Silicon nitride (Si3N4) ceramics have been considered for various components of nuclear power plants such as mechanical seal of reactor...
259
Authors: Shu Ai Shao, Hui Zhi Xi, Yun Peng Chang
Abstract:The erosion and salt spray corrosion–erosion cyclic properties of TC4 titanium are systematically studied in this paper. 1Cr11Ni2W2MoV...
2409
Authors: Bing Ying Wang, Zhen Tong Sun
Abstract:Four different metal coatings of pure aluminum, aluminum zinc alloy, titanium, aluminum Titanium were prepared on the surface of X80 pipeline...
533
Authors: Xiao Ming Cao, Peng Fei Yin, Rui Na Ma
Chapter 11: Materials Behavior
Abstract:Fe-B alloys with different boron contents were dipped into a pure molten zinc bath to investigate their anti-corrosion property. Scanning...
3051
Authors: Feng Jun Lang, Ying Ma, Jian Rong Liu, Xian Qiu Huang, Mou Cheng Li
Chapter 1: Surface Engineering/Coatings
Abstract:The influence of passivation on pitting corrosion of 316L stainless steel in concentrated seawater was investigated by using cyclic anodic...
127