Paper Title:
Preparation of Porous ZrO2-Al2O3 Composite Ceramic with High Strength and Good Corrosion-Resistance
  Abstract

In order to develop porous ceramics with high strength and corrosion resistance as the support for the preparation of asymmetric ceramic membranes, porous ZrO2-Al2O3 composite is designed and fabricated by adding Zr(OH)4.as sintering aid. The content of Zr(OH)4, the sintering temperature and the bending strength before and after corrosion of the composite are discussed. The results shows that 10wt% ZrO2-10wt% Zr(OH)4 -80wt%Al2O3 composite bar fabricated by cold press with the porosity of 32% can be fabricated in 1550°C for 4 h. The bending strength of the composite is 111.2MPa. After corrosion, the quality lose and the bending strength lose is no more than 1%. The tubular composite is suit for the preparation of micro-filtration membrane.

  Info
Periodical
Advanced Materials Research (Volumes 197-198)
Edited by
Huaiying Zhou, Tianlong Gu, Daoguo Yang, Zhengyi Jiang, Jianmin Zeng
Pages
1545-1548
DOI
10.4028/www.scientific.net/AMR.197-198.1545
Citation
Q. B. Chang, X. Q. Liu, X. Wang, Y. Q. Wang, J. E. Zhou, "Preparation of Porous ZrO2-Al2O3 Composite Ceramic with High Strength and Good Corrosion-Resistance", Advanced Materials Research, Vols. 197-198, pp. 1545-1548, 2011
Online since
February 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: X.D. Li, Larry Wang, Tetsuhiko Onda, T. Akao, Motozo Hayakawa
Abstract:Centrifugal casting method was used to fabricate composites with graded structures in alumina-zirconia system. The composition profiles of...
293
Authors: Won Seung Cho, Yeon Chul Yoo, Chin Myung Whang, Nam Hee Cho, Woon Suk Hwang, Jun Gyu Kim, Young Jae Kwon
Abstract:Porous alumina bodies were successfully prepared by spark plasma sintering of alumina powders with different amounts of graphite, and by...
1056
Authors: R. Svinka, V. Svinka, G. Bula, T. Juettner, E. Palcevskis
Abstract:Light weight materials are produced according to the aerated concrete technology using slurries. In concentrated suspensions pore formation...
2266
Authors: Bao Yu Du, Bo Zhao, Tie Lin Duan
Chapter 6: Mechanical Design and Manufacture Technology (2)
Abstract:Physical and mechanical properties as well as microstructure of zirconia toughened alumina ceramics with different zirconia content were...
485
Authors: Qi Bing Chang, Ke Yang, Xia Wang, Ke Kai Cheng, Yong Qing Wang, Jian Er Zhou
Chapter 1: Raw Materials and Processing
Abstract:The high sintering temperature of Al2O3 is the main reason of the high cost of the common ceramic membrane supports. To...
56