Investigation of Phase Composition and Microstructure of the FeAl Intermetallics Compounds Bulks Fabricated by Mechanical Alloying Process and Hot-Pressing Process
  Abstract

The FeAl intermetallics compounds bulks were fabricated by hot-pressing process. The FeAl intermetallics compounds powders were fabricated by mechanical alloying and heat treatment process. The phase composition and microstructure of the FeAl intermetallics compounds powders produced by mechanical alloying and heat treatment were investigated. The phase composition and microstructure of the FeAl intermetallics compounds bulks fabricated by hot-pressing process were investigated. The XRD patterns results showed that the Fe-Al intermetallics compounds powders were fabricated by mechanical alloying for 60h. The FeAl intermetallics compounds powders were fabricated by heat treatment process at 800oC, 900oC and 1000oC. The microstructure showed that the mean particles sizes of the Fe-Al intermetallics compounds powders produced by mechanical alloying decreased remarkably with the increase of milling time. The microstructure showed that the mean particles size of the Fe-Al intermetallics compounds powders produced by mechanical alloying and heat treatment was rather fine and about 4-5μm. The FeAl intermetallics compounds bulks were fabricated by hot-pressing process at 1100oC for 2h under the pressure of 35MPa. The XRD patterns results showed that there existed the FeAl intermetallics compounds phase in sintered bulks. The FeAl intermetallics compounds bulks exhibited the homogenous and compact microstructure. The mean particles size of the FeAl intermetallics compounds was about 2-3μm. The FeAl intermetallics compounds bulks exhibited the high relative density. The FeAl intermetallics compounds bulks with the high relative density were fabricated by hot-pressing process.

  Info
Periodical
Advanced Materials Research (Volumes 228-229)
Edited by
Quanjie Gao
Pages
899-904
DOI
10.4028/www.scientific.net/AMR.228-229.899
Citation
T. Jiang, "Investigation of Phase Composition and Microstructure of the FeAl Intermetallics Compounds Bulks Fabricated by Mechanical Alloying Process and Hot-Pressing Process", Advanced Materials Research, Vols. 228-229, pp. 899-904, 2011
Online since
April 2011
Authors
Export
Price
$35.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Sung Yeal Bae, In Sup Ahn, Ho Jung Cho, Chul Jin Kim, Dong Kyu Park
Abstract:TiC particulate reinforced Fe matrix composite compacts with controlled interfacial reaction was processed by spark plasma sintering after...
217
Authors: Tao Jiang
Abstract:The Fe3Al/Al2O3 composites were fabricated by plasma active sintering process. The Fe3Al intermetallics compounds powders were fabricated by...
1458
Authors: Tao Jiang
Materials Engineering
Abstract:The Fe3Al intermetallics compounds bulks were fabricated by hot-pressing process in this research. The Fe3Al...
1707
Authors: Tao Jiang, Ke Wei Pan
Abstract:Fe3Al/Al2O3 composites were fabricated by pressureless sintering in this research. Fe3Al intermetallics compounds powders were fabricated by...
411