Paper Title:
Effect of Naphthalene Based Superplasticizers on Performance of Ultrafine White Cement
  Abstract

The compressive strength of ultrafine white cement samples at three ages: 3, 7 and 28 days and micro appearance of hydrates were tested. The influence of the usage of superplasticizers on the compressive strength of ultrafine white cement paste and hydrates were investigated. The results indicated that the 28d compressive strength of ultrafine white cement with 3% naphthalene based superplasticizers added was 92.9 MPa, 22.9% of that of pure ultrafine white cements (75.6 MPa). The addition of superplasticizers was beneficial to the density of white cement paste. A large number of hydrates (AFt, C-H-S, and so on) were generated in the capillary pores, which would improve the structure of capillary pores of hardened cement paste, increase the density and strength.

  Info
Periodical
Advanced Materials Research (Volumes 250-253)
Edited by
Guangfan Li, Yong Huang and Chaohe Chen
Pages
182-187
DOI
10.4028/www.scientific.net/AMR.250-253.182
Citation
W. J. Guo, G. X. Du, Q. Xue, J. H. Liao, "Effect of Naphthalene Based Superplasticizers on Performance of Ultrafine White Cement", Advanced Materials Research, Vols. 250-253, pp. 182-187, 2011
Online since
May 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Dong Lin, Yong Quan Lin, Su Hong Yin, Zi Yun Wen
Abstract:The strength and shrinkage properties of mortars with different superplasticizer were studied. The results indicated that the saturation...
155
Authors: Xu Yan Song, Jing Yun Han, Zhi Hai Gao
Chapter 2: Frontiers of Building Materials
Abstract:Through determining Ca(OH)2 content and chemically combined water content, hydration degree of cement with added-calcium thermal...
833
Authors: Martin Boháč, Radoslav Novotný, Jakub Tkacz, Miroslava Hajdúchová, Martin Palou, Theodor Staněk
Chapter 2: Chemistry of Silicates
Abstract:The role of temperature of metakaolin/Portland cement binary system was studied by isothermal calorimetry. Sample with 50 % of metakaolin...
51