Surface Roughness of Cu-Be Alloy (C17200) Rod Alloy Produced by Horizontal Type Continuous Casting Process
  Abstract

Cu-Be alloy (C17200) rod having diameter of 23.5mm was produced by a vacuum continuous casting method at furnace temperature range of from 1240°C to 1260°C with casting speed range of from 35mm/min to 103mm/min. When the furnace temperature was 1240°C and 1250°C, Cu-Be alloy rod without fracture could successfully produced at high casting speed of 103mm/min. However, when the furnace temperature was 1260°C, the breakout occurred at casting speed faster than 78mm/min. Surface roughness (Ra) increased with increasing not only a furnace temperature but also a casting speed.

  Info
Periodical
Advanced Materials Research (Volumes 26-28)
Edited by
Young Won Chang, Nack J. Kim and Chong Soo Lee
Pages
551-554
DOI
10.4028/www.scientific.net/AMR.26-28.551
Citation
S. K. Lee, H.S. Lee, S. C. Lim, T.K. Jung, K.H. Kim, H. C. Kwon, W.M. Jung, "Surface Roughness of Cu-Be Alloy (C17200) Rod Alloy Produced by Horizontal Type Continuous Casting Process", Advanced Materials Research, Vols. 26-28, pp. 551-554, 2007
Online since
October 2007
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Zhi Min Zhang, Qiang Wang, B.C. Li, X. Zhang
Abstract:Warm compression tests of AZ31 Mg alloy were carried out at five temperatures in 30°C intervals from 210°C to 330°C. The samples of...
1813
Authors: Hyeon Taek Son, J.M. Hong, Ik Hyun Oh, Jae Seol Lee, T.S. Kim, Kouichi Maruyama
Abstract:Mg97Zn1Y2 alloy powders were prepared from gas atomization process, followed by consolidation using spark plasma sintering (SPS) process....
1517
Authors: Yi Guo Song, Feng Chen, Li Li, Yu Feng Zheng
Abstract:The advanced manufacturing technology of TiNiNb wide hysteresis shape memory alloy fastener ring was performed by using the tungsten inert...
529
Authors: Bao Hong Zhu, Bai Qing Xiong, Yon Gan Zhang, Udo Fritsching, Ji Shan Zhang, Feng Wang, Zhi Hui Li, Hong Wei Liu
Abstract:A high Zn content Al-Zn-Mg-Cu alloy was prepared by spray forming process and the precipitate behavior and microstructure of the extruded...
481
Authors: Rupa Dasgupta, Satyabrata Das, Amol Kumar Jha
Friction and Wear in Material Processing
Abstract:Metal Matrix Composite made from Al-7075 based alloy dispersed with 10% SiC particles through the liquid metallurgy route were evaluated for...
555