Reaction Behavior of Phosphorus in CaO-SiO2-FeOx Low Basicity Slag
  Abstract

For investigating the reaction behavior of phosphorus in CaO–SiO2–FeOx low basicity slag, the CaO–SiO2–FeOx slag containing various amount of CaO particles was heated at 1623K and 1673K, respectively for 10 to 600s, and the products formed at the interface of the CaO particles and molten slag were observed by scanning electron microscopy (SEM) with energy dispersive X-ray (EDX). The research results showed that the solid solution containing P2O5 increased with the increasing of the heating temperature, and the formation of condensed phase was promoted by increasing the holding time and the CaO solid proportion.

  Info
Periodical
Advanced Materials Research (Volumes 282-283)
Chapter
Chapter 1: Material Engineering, Chemistry, Bioinformatics
Edited by
Helen Zhang and David Jin
Pages
129-132
DOI
10.4028/www.scientific.net/AMR.282-283.129
Citation
C. Su, J. K. Yu, N. N. Lv, "Reaction Behavior of Phosphorus in CaO-SiO2-FeOx Low Basicity Slag", Advanced Materials Research, Vols. 282-283, pp. 129-132, 2011
Online since
July 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Jin Shu Cheng, Hui Guang Qiu, Li Ying Tang
Abstract:Much phosphorus slag which is produced every year, not only brings about the resource waste, but also results in the pollution of the...
37
Authors: Zai Bo Li, San Yin Zhao, Xu Guang Zhao, Tu Sheng He
Building Materials
Abstract:To realize the industrial application of online reconstruction technique of steel slag, a pilot-scale reconstruction research of steel slag...
906
Authors: Hui Ding, Yan Jin, Zhi Bing Tian, Dan Jiang Wu
Chapter 4: Metallurgy Materials and Environmental Engineering
Abstract:In this paper, CaO-Fe2O3-CaCl2 and CaO-Fe3O4-CaCl2 system dephosphorizer...
354
Authors: Wei Xiang Wang, Zheng Liang Xue, Sheng Qiang Song, Ping Li, Zhi Chao Chen
Chapter 2: Iron and Steel
Abstract:The basic thermodynamic analysis of silicothermic reduction during direct alloying to smelting vanadium steel with V2O5...
164
Authors: Ding Guo Zhao, Shu Huan Wang, Ming Jian Guo
Chapter 4: Material Engineering and its Application Technology
Abstract:The sample of oxide inclusion was obtained in the different stage of steelmaking for the 65 steel. The microstructure was observed by using...
324