Paper Title:
Heat Treatment of Heavy Forgings with diameter 1700mm
  Abstract

In order to establish a suitable heat treatment process after forging for the heavy forgings to prevent “grain inheritance”, a heat treatment process including pretreatments, pre-heating, normalization, super-cooling and dehydrogenation is proposed. The heavy forgings with the ratio 1.3 of largest diameter 1700mm to its length 1260mm are manufactured by two times upsetting and elongating process. The results show that the heavy forgings treated according to the forging process and the heat treatment process are all qualified and up to the standards of supersonic inspection.

  Info
Periodical
Advanced Materials Research (Volumes 284-286)
Chapter
Other related topics
Edited by
Xiaoming Sang, Pengcheng Wang, Liqun Ai, Yungang Li and Jinglong Bu
Pages
2388-2391
DOI
10.4028/www.scientific.net/AMR.284-286.2388
Citation
J. H. Su, X. F. Liu, Y. Y. Chen, Y. L. Shi, "Heat Treatment of Heavy Forgings with diameter 1700mm", Advanced Materials Research, Vols. 284-286, pp. 2388-2391, 2011
Online since
July 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: B.Z. Bai, Y. Yu, D.Y. Liu, J.L. Gu
Abstract:A novel carbide free bainite/martensite (CFB/M) high strength steel of 1500MPa grade is micro-alloyed with Nb in order to refine the...
3140
Authors: J.M. Rodriguez-Ibabe, P. Uranga, B. López
Keynotes
Abstract:The microstructural heterogeneities in steels may have different origins. The tendency in industry to decrease the total amount of reduction...
157
Authors: Jin Ming Liu, Jie Liu, Guang Wei Fan, Dong Fang Du, Guo Ping Li, Cheng Jun Chai
A. Environment Related Materials and Photocatalysts
Abstract:Effect of solution treated temperature at 5001100°C on ferrite/austenite ratio and σ phase precipitation has been studied in this paper, and...
3
Authors: Wen Ping Liu, B. Zhang, Pei Qi Wang, Qin He Zhang
Chapter 13: Materials Forming
Abstract:To improve the product properties of H-beams, it is essential to understand the effects of hot rolling parameters on the microstructure...
2024
Authors: Peng Chen, Yun Bo Xu, Xiao Long Yang, Hong Liang Yi, Guo Dong Wang
Abstract:In this work, the bainite transformation during isothermality of aluminium bearing TRIP steel was studied by dilatometric experiment on a...
237