Development and Evaluation of a High-Strength and Anti-High Temperature Pre-Crosslinking Gel
  Abstract

There are many kinds of pre-crosslinking gel being used at present, but their high temperature resisting performance are poor. The general temperature resisting capacity is only about 120°C. Aiming at the poor resistance to high temperature of current pre-crosslinking gel , an anti-high temperature pre-crosslinking polymer gel is developed in this paper. Experimental results show that this product has appropriate swelling ability, better anti-extruding strength, better deformability and elasticity. The temperature resisting capacity in freshwater can reach as high as 150°C,and it still has comparatively higher strength after high temperature treatment.

  Info
Periodical
Advanced Materials Research (Volumes 295-297)
Chapter
Chapter 1: Materials Properties
Edited by
Pengcheng Wang, Liqun Ai, Yungang Li, Xiaoming Sang and Jinglong Bu
Pages
1221-1224
DOI
10.4028/www.scientific.net/AMR.295-297.1221
Citation
K. H. Lv, T. Shi, D. Z. Zhu, Y. Liu, W. G. Qiao, "Development and Evaluation of a High-Strength and Anti-High Temperature Pre-Crosslinking Gel", Advanced Materials Research, Vols. 295-297, pp. 1221-1224, 2011
Online since
July 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Ana Vera Machado, Martin van Duin, José A. Covas
Abstract:Dynamic vulcanisation of EPDM/PE blends using the resol/SnCl2 system was studied in a co-rotating twin screw extruder using a series of...
838
Authors: Qun Feng Liu, Bo Yuan, Xiao Feng Chen
Abstract:A kind of poly(N-isopropylacrylamide) (PNIPAM) gel was synthesized by radical polymerization of N-isopropylacrylamide monomer in the present...
1483
Authors: Long Gui Peng, Guang Cheng Zhang
Chapter 2: Biochemical Materials, Environmental Materials and Chemistry Processing
Abstract:By graft copolymerization of calcium lignin sulphonate with acrylic acid and acrylamide,high water absorption and retention material was...
391
Authors: Fayezeh Eslami, Zuraida Ahmad, Nur Humairah Abdul Razak
Chapter 8: Nanomaterials and Nanotechnology
Abstract:Hydrogel based on petroleum polymer are expensive, non-biodegradable and non-decompose which lead them to heavy waste in environment. In this...
390
Authors: Kantima Chaochanchaikul, Wanlop Harnnarongchai
Chapter 1: Ceramics, Semiconductors and Composites
Abstract:The aim of this work was to compare and discuss the influence of multifunctional monomers as crosslinking agent (Triallyl Isocyanurate; TAIC)...
59