Study on the Brazing Technology and Mechanical Properties Using bmp7 Filler Metal
  Abstract

The 1Cr18Ni9Ti stainless steel was brazed in the argon shield and впр7 as the filler metal. The spreadability and clearance fillability of впр7 on 1Cr18Ni9Ti stainless steel was evaluated at different temperatures and the optimum brazing temperature was clearly demonstrated as 1170~1190°C. Scanning electron microscope (SEM) study combined with energy dispersive spectrometer (EDS) showed the presence of many undissolved elements and voids in the joints while the brazing clearance is 0.15mm, which directly caused a low joint shearing strength. Almost no undissolved brittle compounds were observed while the brazing clearance stands in a range of 0.01mm~0.10mm. Therefore, a Ni-based solid solution with good performance was obtained in the joint. Those brazing parameters matching with the holding time 8~10min could bring the joint a typical performance which fully satisfies Russian standard. These conclusions had been proved by joint stress-rupture and low cycle fatigue tests.

  Info
Periodical
Advanced Materials Research (Volumes 295-297)
Chapter
Chapter 5: Joining Processes and Equipment
Edited by
Pengcheng Wang, Liqun Ai, Yungang Li, Xiaoming Sang and Jinglong Bu
Pages
1879-1884
DOI
10.4028/www.scientific.net/AMR.295-297.1879
Citation
X. Z. Hua, W. T. Guo, Y. T. Xu, Z. G. Ye, A. H. Zou, X. L. Zhou, "Study on the Brazing Technology and Mechanical Properties Using bmp7 Filler Metal", Advanced Materials Research, Vols. 295-297, pp. 1879-1884, 2011
Online since
July 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: W.K. Joo, Yi Qi Wang, H.T. Yang, W.C. Lee, C.Y. Sim, Jung I. Song
Abstract:The microstructures and mechanical properties of OFHC copper/STKM 11A for D-tube joints brazed using BAg filler metal at 870 °C for 20...
1345
Authors: Hong Tao Zhang, Bo Chen, Ming Zhi Zhai, Lei Li
Abstract:Joining Cu to Al has been carried out by high-frequency induction brazing without filler metal. Experimental results showed that the eutectic...
2539
Authors: Xing Hua Liang, Xiao Hua Jie
Other related topics
Abstract:The microstructure and properties of brazing weld of 3003 Aluminum Alloy has been studied by using the methods of microstructure...
3098
Authors: Zhuo Jun Chen, Chang Jin Yang, Xiao Long Gu, Cheng Dong Wu, Long Long Feng
Chapter 3: Materials Forming, Machining and Joining
Abstract:Vacuum brazing of 316L stainless steel with BNi-2 brazing filler metal.The effects of brazing temperature and brazing clearance on...
1242
Authors: Zhuo Jun Chen, Ming Wang, Long Long Feng
Chapter 13: Surface Engineering/Coatings
Abstract:To study the effect of brazing clearance and temperature on strength and microstructure, vacuum brazing of 316L stainless steel was carried...
1890