Influence of Annealing Temperature on Properties and Texture of High Strength IF Steel
  Abstract

Using the cold rolled High Strength IF Steel sheet of 1.0 mm thickness as the test material,the r value and recrystallization texture were investigated by the tensile test and X Radial Diffraction Device.The results show that the test steel were annealed by heating to 760°C,800°C,840°C and holding sixty seconds,and with the increase of the annealing temperature ,the recrystallization finished and the texture to obtain the full evolution,and the r value of the steel grown.After the annealing,the recrystallization texture shows strong γ-fiber texture,homogeneous γ-fiber and weak α-fiber texture,and the texture strength change rule with the annealing temperature change was gained.

  Info
Periodical
Advanced Materials Research (Volumes 311-313)
Chapter
Steel and Iron
Edited by
Zhongning Guo
Pages
940-943
DOI
10.4028/www.scientific.net/AMR.311-313.940
Citation
K. H. Hu, S. B. Zhou, D. X. Tian, G. W. Feng, "Influence of Annealing Temperature on Properties and Texture of High Strength IF Steel", Advanced Materials Research, Vols. 311-313, pp. 940-943, 2011
Online since
August 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: T. He, Y.D. Liu, Yan Wu, Q.W. Jiang, Gang Wang, Yan Dong Wang, Liang Zuo
Abstract:An experimental setup was designed to study the recrystallization kinetics of Interstitial Free (IF) steel in this work. The 80% cold rolled...
417
Authors: Ranjit Kumar Ray, P. Ghosh
Chapter 1: Keynotes
Abstract:Interstitial free high strength steels (IFHS) are widely used in the automobile sector due to their high strength and excellent formability....
34
Authors: Zhi Gang Wang, Zheng Zhi Zhao, Ai Min Zhao, Jie Yun Ye
Chapter 2: Manufacturing and Design Science
Abstract:Deep drawing dual phase steel was designed and trial-produced in the laboratory. The microstructure and recrystallization texture was studied...
1223
Authors: Jie Yun Ye, Zheng Zhi Zhao, Zhi Gang Wang, Ai Min Zhao, Jing Jing Chen
Chapter 3: Iron and Steel
Abstract:C-Mn-Cr-Mo dual phase steel was piloted in laboratory. OM, SEM, tensile tests and XRD were used to characterize the microstructures,...
670
Authors: Ho Jun Bang, Ha Guk Jeong, Jong Beom Lee
B. Eco-Materials Processing and Design, Multifunctional Materials
Abstract:Mg alloy sheets exhibit the yield strength of 280 MPa and elongation of 18 % by rolling at 423 K. Elongation of Mg alloy sheets was improved...
190