The Effect of Electrospinning Parameters on Mophology of PAN/PU Composite Nanofibers
  Abstract

The PAN/PU nanofiber membrane was prepared by twin-jet electrospinning. By changing the spinning voltage, solidification distance and jet velocity, the effects of each parameter on the fiber morphology could be analyzed. The diameter of the fiber was examined by scanning electron microscopy. The result showed that the excellent product could be got under such experimental conditions, which were 10%PAN and 10%PU solution, 25KV voltage, 15cm solidification distance with the jet velocity of 0.8ml/h and 1.3ml/h.

  Info
Periodical
Advanced Materials Research (Volumes 332-334)
Chapter
Chapter 8: Structure, Properties and Processes of Non-Woven Materials
Edited by
Xiaoming Qian and Huawu Liu
Pages
1343-1346
DOI
10.4028/www.scientific.net/AMR.332-334.1343
Citation
J. Shi, D. Jia, B. W. Cheng, W. M. Kang, "The Effect of Electrospinning Parameters on Mophology of PAN/PU Composite Nanofibers", Advanced Materials Research, Vols. 332-334, pp. 1343-1346, 2011
Online since
September 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Wei Min Kang, Bo Wen Cheng, Quan Xiang Li, Xu Pin Zhuang
Abstract:A kind of novel biodegradable poly(hexamethylene adipate) (PHMA) nanofibers with diameter of 100~700nm using a mixed solvent of...
555
Authors: Todsapon Nitanan, Praneet Opanasopit, Prasert Akkaramongkolporn, Theerasak Rojanarata, Tanasait Ngawhirunpat
Abstract:This study focused on the preparation of electrospun polystyrene (PS) nanofibers. Polystyrene solutions were prepared in single...
629
Authors: Guang Yang, Zhi Jiang Cai
Chapter 10: Finishing Technology
Abstract:Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) (P3HB-co-4HB) nanofiber membranes were papered via electrospinning from polymer solution. The...
1527
Authors: En Zhong Li, Da Xiang Yang, Wei Ling Guo, Hai Dou Wang, Bin Shi Xu
Chapter 2: Micro / Nano Materials
Abstract:Ultrafine fibers were electrospun from polyacrylonitrile (PAN)/N,N-dimethyl formamide (DMF) solution as a precursor of carbon nanofibers. The...
642
Authors: Si Yu Li, Yan Wei Wang, Tan Wen Jun
Chapter 4: Material Science and Technology
Abstract:PAN and P(AN-co-MA) nanofibers have been successfully prepared by electrospinning. The mass concentration is 6%-12%, voltage of 15-25 kV,...
1042