The Exploration on Synthesis of Calcium Aluminate and Fe-Si Alloys Using Red Mud and Aluminum Dross
  Abstract

Calcium aluminate and Fe-Si alloys were successfully synthesized by using red mud and aluminate dross as the main raw materials in the lab-scale experiment. Three apt experimental parameters were obtained: 1.2 times of theoretical addition amount of aluminum dross, binary basicity of raw materials 0.9, 40min smelting time. The chemical compositions of calcium aluminate synthesized meet the standard of CA-60 cement of China, and the calcium aluminate can be used as pre-melted-slag in Steelmaking process.

  Info
Periodical
Advanced Materials Research (Volumes 97-101)
Edited by
Zhengyi Jiang and Chunliang Zhang
Pages
1104-1108
DOI
10.4028/www.scientific.net/AMR.97-101.1104
Citation
J. B. Hu, Y. B. Li, K. D. Wu, F. Liu, Q. Zhu, Y. W. Li, "The Exploration on Synthesis of Calcium Aluminate and Fe-Si Alloys Using Red Mud and Aluminum Dross", Advanced Materials Research, Vols. 97-101, pp. 1104-1108, 2010
Online since
March 2010
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Cai Jun Zhang, Li Guang Zhu, Dong Mei Tu, Shuo Ming Wang, Hui Ding
Abstract:By means of the thermodynamics analysis of inclusion modification in the process of calcium treatment, and the advantage area chart of...
1659
Authors: Jin Hong Li, Ling Xin Tong, Wen Cai Zhou
Abstract:A new type aluminous cement containing magnesium aluminate (MA) spinel was prepared from mixtures of limestone, magnesian and bauxite at...
467
Authors: Zhi Fang Tong, Sen Lin Xie, Li Heng Zhang, Tao Chen, Wei Liu, Gui Huan An
Chapter 3: Metallurgy of Non-Ferrous Metals
Abstract:For the low m(Al2O3)/m(SiO2) (mass ratio, for short A/S) calcium aluminate slag obtained from smelting...
288
Authors: Wen Ping Li, Jun Hong Chen, Christoph Wohrmeyer, Hong Yan Guan, Jia Lin Sun
Chapter 3: Materials Processing Technology
Abstract:Melting properties of CaO-Al2O3-SiO2-MgO system calcium aluminate (CA) flux were investigated through orthogonal design on three levels of...
569
Authors: Sureerat Polsilapa, Nakarin Sriyowong
Chapter 1: Materials and Technologies of Chemical Industry
Abstract:This project researched a mechanism of the decomposition of zinc ferrite (ZnFe2O4) to be zinc oxide (ZnO) and calcium...
72