The Influence of Starting Mass Grain Size Distribution on Magnesia-Spinel Products Microstructure
  Abstract

The paper presents the results of investigations on the influence of the starting mass grain size distribution on microstructure of sintered magnesia-spinel products. The model investigation was conducted using magnesia clinkers and fused spinel. The grain size distribution of starting mixes were selected according to Dinger and Funk's theoretical curves with different values of n coefficient. The results clearly indicate that the best properties were achieved when n value changed in the range of 0.22 - 0.30 and forming pressure was contained in the range of 160 - 200 MPa.

  Info
Periodical
Edited by
P. VINCENZINI
Pages
2292-2297
DOI
10.4028/www.scientific.net/AST.45.2292
Citation
J. Szczerba, Z. Pędzich, "The Influence of Starting Mass Grain Size Distribution on Magnesia-Spinel Products Microstructure", Advances in Science and Technology, Vol. 45, pp. 2292-2297, 2006
Online since
October 2006
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Jacek Szczerba
Abstract:The paper describes formation of the phases in magnesia-zirconia refractories due to reaction with the cement furnace charge in a form of...
15
Authors: Chao Nan Yin, Ling Chao Lu, Shou De Wang, Ya Ming Chen
Abstract:The influence of MgO on the composition, structure and properties of alite-calcium strontium sulphoaluminate cement were investigated by...
472
Authors: Qiang Song, Bao Jing Shen, Zhi Jun Zhou
Abstract:Under different content of blast furnace slag and steel slag powder, cements were mixed to investigate the effect of dosage of these two...
17
Authors: Jian Cheng An, Lin Jun Wang, Yun Sheng Feng
Building Materials
Abstract:The Bauxite-based Homogenized Grog (BHG) was industrial producted using bauxite with about 70 wt.% Al2O3 as starting...
1079
Authors: Guo Xiang Yin, Yong Li, Jun Hong Chen, Bo Pan
Chapter 9: Environmental Friendly Materials
Abstract:The structure and properties of iron-rich magnesia-spinel composite prepared using sintered iron-rich magnesia and MgO-rich spinel for...
1915