Paper Title:
Experimental Study on the Osteoinduction of Calcium Phosphate Biomaterials In Vivo and the Capability of Supporting Osteoblast Proliferation In Vitro
  Abstract

The purpose of this study was to evaluate the response of osteoblasts to the calcium phosphate with different surface modification, and to evaluate the osteoinductive capabilities of these biomaterials. 60HA/40α-TCP ceramics sintered at 1250oC was applied in this study. The ceramic cylinder with F5mm×8mm and slice with F10mm×1mm were prepared respectively. One thirds of the ceramics were formed bone-like apatite (BLA), and the surface of another one thirds was modified with collagen. Osteoblasts (1×106/ml) were co-cultured with the three kinds of thin slices for 12h, 24h and 48h. SEM observation was applied to evaluate if the surface modification and BLA formation could affect the attachment and proliferation of osteoblast in vitro. The three kinds of cylinder samples were implanted in dog muscle to evaluate their differences in osteoinduction. Cells grew in multi-layers and well attached to the surface and proliferated well in the group of collagen and HA/TCP. In untreated and BLA precipitated group, cells did not attach to the surface well. Osteoinduction was good in BLA precipitated group and the amount of bone formed was higher; in untreated group and collagen-treated group, no bone formation was observed in the tested period. This result indicated that the scaffold used in cell-materials composites in vitro and that in osteoinductive material based tissue engineering in vivo was not same.

  Info
Periodical
Key Engineering Materials (Volumes 284-286)
Main Theme
Edited by
Panjian Li, Kai Zhang and Clifford W. Colwell, Jr.
Pages
293-296
DOI
10.4028/www.scientific.net/KEM.284-286.293
Citation
C.Y. Bao, P. Li, Y. F. Tan, Y. Cao, X.Y. Ling, C. L. Deng, X. D. Li, W.C. Chen, H. S. Fan, X. D. Zhang, "Experimental Study on the Osteoinduction of Calcium Phosphate Biomaterials In Vivo and the Capability of Supporting Osteoblast Proliferation In Vitro ", Key Engineering Materials, Vols. 284-286, pp. 293-296, 2005
Online since
April 2005
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: C.Y. Bao, P. Li, Yan Fei Tan, Y. Cao, Xiao Yan Lin, Chun Lin Deng, Xu Dong Li, Guo Min Ou, W.C. Chen, P. Gong, Hong Song Fan, Xing Dong Zhang
Abstract:The purpose of this study was to evaluate the response of osteoblasts to calcium phosphate with different surface modification, and to...
281
Authors: Qiu Lian Dai, C.Q. Qin, Xipeng Xu
Abstract:In this paper, three kinds of granite were lapped and polished by loose abrasives. Glossiness and surface roughness of the lapped and...
305
Authors: Kien Woh Kow, Rozita Yusoff, A. R. Abdul Aziz, E. C. Abdullah
Chapter 23: Thermal Engineering Theory and Applications
Abstract:Silica aerogel with extremely low thermal conductivity has great potential to be used as thermal insulating material. Opacification using...
2482
Authors: Jin Yang Lin, Zhuo Ying Zhang
Chapter 17: Agricultural Products Processing and Biological Pharmaceutical
Abstract:The present study was carried out to investigate anti-hypoxia and anti-fatigue activities of flavonoids from bark of Eucommia ulmoides...
1608