Paper Title:
Aluminum Borate Whiskers Growing by Compensation of TiB2
  Abstract

Aluminum borate whiskers with TiB2 as borate source were prepared in this paper. The phase transformation process was analyzed by XRD and TG-DSC. The results indicate that TiB2 was decomposed into TiO2 and B2O3 in the calcining process in the active [O] atmosphere. 2Al2O3.B2O3 was formed in the lower temperature with reaction of Al2O3 and B2O3, while 9Al2O3.2B2O3 whiskers were grown by compensation of 2Al2O3.B2O3 at higher temperature (above 1050oC)

  Info
Periodical
Edited by
Chi Y.A. Tsao and Jing Kun Guo
Pages
115-120
DOI
10.4028/www.scientific.net/KEM.313.115
Citation
D. M. Zhang, Y. J. Li, L. M. Zhang, J. K. Guo, "Aluminum Borate Whiskers Growing by Compensation of TiB2 ", Key Engineering Materials, Vol. 313, pp. 115-120, 2006
Online since
July 2006
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Guo Sheng Wang, Kang Jun Wang, Jia Hou, Yu Feng Xu
Abstract:Aluminum borate (Al4B2O9) nanomaterials were synthesized via a sol-gel process using...
3056
Authors: Guo Sheng Wang, Kang Jun Wang, Jia Hou, Ying Ming Wang, Chang Yi Kong
Chapter 2: Mechanical Engineering, Control Engineering and Materials Engineering
Abstract:Magnesium borate ball of wires, nanowires and petaliforms were prepared via calcination of magnesium borate hydroxide synthesized by...
642
Authors: Shuang Jie Song, Xue Ying Nai, Wu Li, Cheng Cai Zhu, Qing Fen Meng
Chapter 4: Micro/Nano Materials
Abstract:A type of calcium borate whiskers with highly thermal stability was synthesized by hydrothermal method at 180 °C for 2 h, using borax,...
693
Authors: Zhao Jun Mo, Jing Lin, Ying Fan, Xing Hua Zhang, Yan Ming Xue, Chun Yong Liang, Hong Shui Wang, Xue Wen Xu, Long Hu, Zhun Ming Lu, Cheng Chun Tang
Abstract:Large quantities of BN-coated aluminum borate (Al18B4O33) nanowhiskers with typical 20 - 50 nm in diameter and 0.5 - 2 m in length have been...
125