Large-Scale Fabrication of Ti3AlC2 Powder with High-Purity
  Abstract

A synthesis method of high-pure Ti3AlC2 powder with a large scale was presented as pressureless synthesis using TiC, Ti and Al powders as starting materials at 1300~1450°C in flow Ar. The different raw material scales were tested from 2 g to 1.0 kg, and the results showed that the purities of Ti3AlC2 powders could be kept around 97 wt% at different scales of raw materials. SEM observation and particle size analysis revealed that the synthesized Ti3AlC2 powders were uniform and around 5 μm in particle size. This method can be used for mass production of Ti3AlC2 powders with high-purity.

  Info
Periodical
Key Engineering Materials (Volumes 336-338)
Edited by
Wei Pan and Jianghong Gong
Pages
948-951
DOI
10.4028/www.scientific.net/KEM.336-338.948
Citation
C. A. Wang, C. Q. Peng, Y. Song, Y. Huang, "Large-Scale Fabrication of Ti3AlC2 Powder with High-Purity", Key Engineering Materials, Vols. 336-338, pp. 948-951, 2007
Online since
April 2007
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Jian Feng Zhu, Guo Quan Qi, Fen Wang, Hai Bo Yang
Abstract:Ti2AlC powders with high purity were successfully synthesized via high energy milling and heat treatment of Ti, C and Al powders. The effects...
340
Authors: Jian Feng Zhu, Na Han, Kun Wang, Fen Wang
Abstract:Elemental mixture of Ti, Al and C was high energy milled in a planetary ball mill under high-purity nitrogen gas protection and then hot...
846
Authors: Jian Feng Tong, Ling Wang, Da Ming Chen
Abstract:A new technology, gel solid-state reaction, for synthesis of SrTiO3 ceramic composite powders is described in the present paper....
78
Authors: Ai Guo Zhou, Liang Li, Tai Chao Su, Shang Sheng Li
Chapter 2: Engineering Ceramics and Ceramic Composites
Abstract:Ti3SiC2, a ternary carbide, was proposed at this paper to use as the binder of polycrystalline diamonds to overcome the...
671
Authors: Peng Xiao, Xiao Yu Zhang, Hong Wei Lu
Chapter 1: Materials Science
Abstract:Cu-1.37Cr alloy powders were prepared by gas atomization process, and the cooling rates of alloy powders were calculated through the...
60