Intergranular Fracture at 500°C in Pre-Fatigue Crack Tip Damaged Zone of Austenitic Stainless Steel
  Abstract

  Info
Periodical
Key Engineering Materials (Volumes 345-346)
Edited by
S.W. Nam, Y.W. Chang, S.B. Lee and N.J. Kim
Pages
453-456
DOI
10.4028/www.scientific.net/KEM.345-346.453
Citation
Y. Iino, "Intergranular Fracture at 500°C in Pre-Fatigue Crack Tip Damaged Zone of Austenitic Stainless Steel ", Key Engineering Materials, Vols. 345-346, pp. 453-456, 2007
Online since
August 2007
Authors
Export
Price
$35.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Yoichi Kayamori, S. Hillmansen, P.S.J. Crofton, Roderick A. Smith
Abstract:Static and dynamic ductile crack propagation tests were carried out using thin single edge notched tension (SENT) specimens of...
2180
Authors: Won Beom Kim, Jeom Kee Paik
Abstract:In this research, corrosion fatigue tests using 490MPa TMCP steel were performed in synthetic seawater condition to investigate the...
1043
Authors: Won Beom Kim, Jeom Kee Paik
Abstract:In this research, corrosion fatigue tests using tensile strength of 490MPa TMCP steel were performed in synthetic seawater condition to...
1145
Authors: Wei Tang, He Xue, Dan Zhao
Abstract:Environmentally assisted cracking (EAC) or stress corrosion cracking (SCC) of key structural materials in the environments of the light water...
1128
Authors: M.R.M. Aliha, Mahdi Rezaei
Abstract:Crack growth path was investigated experimentally, numerically and theoretically using two test specimens subjected to pure mode II loading....
159