Comparison of Property of Dynamic Melting-Loss H13 Steel by Different Surface Treatment
  Abstract

In order to prolong the service life of Aluminum alloy die casting dies, different surface treatments were adopted to avoid melting loss on the surface of the dies. In this paper, the dynamic melting-loss properties of H13 steel were compared among non-treatment, vapor oxidation treating, carbonitriding and composite treatment of nitirding and vapor oxidation in liquid aluminum of ADC12 at 700 °C by the weight loss method. The surface structures of the specimens after treatments were analyzed by the optical microscopy (OP); the patterns of specimens on the surface were observed by measuring microscope and the melting-loss characteristics of specimens with different treatment were analyzed. The results showed that the melting-loss property was heightened obviously by different surface treatments; especially the melting-loss property of the specimens with composite treatment of nitirding and vapor oxidation was the best.

  Info
Periodical
Key Engineering Materials (Volumes 353-358)
Edited by
Yu Zhou, Shan-Tung Tu and Xishan Xie
Pages
2155-2158
DOI
10.4028/www.scientific.net/KEM.353-358.2155
Citation
Y. H. Chen, X. C. Wu, Y. A. Min, "Comparison of Property of Dynamic Melting-Loss H13 Steel by Different Surface Treatment", Key Engineering Materials, Vols. 353-358, pp. 2155-2158, 2007
Online since
September 2007
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: M. Zlatanović, N. Popović, Ž. Bogdanov, A. Kunosić
61
Authors: Chun Yan Nan, Derek O. Northwood, Randy J. Bowers, Xi Chen Sun
Abstract:Carbonitriding is a metallurgical surface modification technique that is widely used in the automotive industry to increase surface hardness...
829
Authors: Xin Mei Li, Xiao Feng Dong, Tu Erxun Si Dike, Kai Jie Li, Dong Yu
Chapter 1: Machining Technologies and Materials Engineering
Abstract:Porous nanocrystalline thick Ti (CxN1-x) films which bond firmly to the substrate are obtained on commercially pure...
152
Authors: Hong Mei Zhu, Ru Shu Peng, Chao Hui Weng
Chapter 17: Materials and Products Manufacturing Technology
Abstract:The 45 steel was processed by laser remelting after the carbonitriding heat treatment in this study. The microstructure morphology and...
2613
Authors: Chuan Xu, Mao Sheng Yang, Ai Qiong Ma, Shan Ju Zheng
Abstract:The carburizing behavior of low-carbon Cr-Ni-Mo, the nitriding behavior of C-Cr-W bearing steel and the carburizing process prior to...
317