The Experimental Study on Wear Performance of Brazed Diamond Grits
  Abstract

The wear resistance samples of brazed single crystal diamond with Ni-Cr filler alloy were prepared, using high frequency induction brazing and vacuum brazing methods. By wear test of brazed single crystal diamond, the wear performance of the samples with different brazing processes was studied. The test result indicates that the wear performance of the high frequency induction brazed diamond samples is better than that of the vacuum brazed diamond samples. Because of different brazing processes, the wearing pattern of diamond varied; the wear course of the vacuum brazed diamond samples in the initial wear period were abnormal and the failure modes is different.

  Info
Periodical
Key Engineering Materials (Volumes 359-360)
Edited by
Jiuhua Xu, Xipeng Xu, Guangqi Cai and Renke Kang
Pages
28-32
DOI
10.4028/www.scientific.net/KEM.359-360.28
Citation
Y. Chen, H. J. Xu, Y. C. Fu, "The Experimental Study on Wear Performance of Brazed Diamond Grits", Key Engineering Materials, Vols. 359-360, pp. 28-32, 2008
Online since
November 2007
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Hui Huang, H.M. Zhu, Xipeng Xu
146
Authors: Jiu Hua Xu, Wen Feng Ding, F. Qian
Abstract:The joining strength and corresponding fracture mechanism of the brazing interface between diamond grains and tool matrix is one of the...
501
Authors: Shu Sheng Li, Jiu Hua Xu, Bing Xiao, Ming Hua Yan, Yu Can Fu, Hong Jun Xu
Abstract:A kind of brazed monolayer diamond grinding wheel was developed with a relatively regular distribution of grains on the wheel surface....
381
Authors: Zhi Bo Yang, Jiu Hua Xu, Ai Ju Liu
Abstract:Brazing diamond grits onto steel substrate using a Ni-based filler alloy was carried out via laser beam in an argon atmosphere. The...
3879
Authors: Zhi Bo Yang, Ai Ju Liu, Jiu Hua Xu
Abstract:Brazing diamond wheel was carried out via laser in an argon atmosphere. The interfacial microstructures among brazed diamond, the filler...
218