Preparation of TiO2-Ni Wear-Resistant Film on Metal Surface
  Abstract

TiO2-Ni wear-resistant film on metal surface is manufactured by electroless composite plating. TiO2 content in the film depends on the concentration of TiO2 particle in the plating liquid. The optimal TiO2 content in the plating liquid is 15-20g/l. TiO2 content in the film is 5-8%. When TiO2-Ni composite film is treated at 200°C, its hardness increases with the prolonging of heat-treatment time. After 10 hours heat-treatment at 200°C, the hardness increases from HV 750 kg/mm2 to HV 1300 kg/mm2.

  Info
Periodical
Key Engineering Materials (Volumes 368-372)
Edited by
Wei Pan and Jianghong Gong
Pages
1284-1286
DOI
10.4028/www.scientific.net/KEM.368-372.1284
Citation
C. H. Li , "Preparation of TiO2-Ni Wear-Resistant Film on Metal Surface", Key Engineering Materials, Vols. 368-372, pp. 1284-1286, 2008
Online since
February 2008
Authors
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Xiao Feng Shang, Zhi Jian Wang, Dong Xue Han, Zhen Tao Xie
Abstract:In the process of metal powder laser rapid forming, various defects may be caused in forming parts on account of technical parameters,...
3726
Authors: Hong Yan Liu, Hui Zhang
Abstract:Shock accumulation damage failure of rock is often seen in engineering at present. The damage model based on stress wave attenuation is...
4262
Authors: Xiao Qin Yi, Qing Hai Zeng, Ying Liang
Chapter 20: Mechanical Behavior and Fracture
Abstract:Simulating motion process of incompact landslip-collapse soil. Monitoring evolution process of average contact force and unbalance force when...
2174