This work aimed to investigate the effect of different sintering routes on properties of Ni-Al2O3 membrane. Alumina powder was mixed with 10 wt% nickel powder by dried ball-milling. Then, the mixture powder was uniaxially pressed to a bar shape and sintered via different sintering conditions. First route, the Ni-Al2O3 specimen was sintered at 1300°C for 2 h under air and then reduced at 900°C for 2 h under H2 atmosphere. Second route, the specimen was sintered at 1300°C for 2 h under argon. After sintering process, the physical and mechanical properties of membrane obtained from two routes were compared and discussed.