Fatigue Crack Growth Rate under Different Bending to Torsion Ratios in 10HNAP Steel
  Abstract

The paper contains the fatigue test results of rectangular cross-section specimens made of 10HNAP steel. The specimen height to width ratio was 1.5. Bending with torsion tests were carried out for the following ratios of bending to torsional moments MaB / MaT = 0.47, 0.94, 1.87 and the loading frequency 26.5 Hz. The tests were performed in a high cycle fatigue regime for the stress ratio R = - 1 and phase shift between bending and torsion loading equal to  = 0.

  Info
Periodical
Edited by
Pavel Šandera
Pages
187-190
DOI
10.4028/www.scientific.net/KEM.465.187
Citation
Z. Marciniak, D. Rozumek, "Fatigue Crack Growth Rate under Different Bending to Torsion Ratios in 10HNAP Steel", Key Engineering Materials, Vol. 465, pp. 187-190, 2011
Online since
January 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: You Tang Li, Ping Ma, Chang Feng Yan, Fu Yuan Lang
Abstract:Safety designs and fracture designs are the two important fields of crack theory. The fracture problems of middle carbon steel under...
1153
Authors: Ryosuke Matsui, Hisaaki Tobushi, Yoshiyasu Makino
Abstract:In this study, we performed the bending fatigue test and investigated the influence of strain ratio on fatigue life in TiNi shape memory...
1193
Authors: Dal Woo Jung, Nak Sam Choi
Abstract:Fatigue fracture behavior of a hybrid joint part for the tilting car body was evaluated in comparison to the case of static fracture. The...
2860
Authors: Guo Jun Wang, Mei Hua Jiang, Shi Shun Zhu, An Tao Xu
Abstract:Bending fatigue is one of the main failure modes of gears. The method of gear fatigue design was discussed in many papers. Most of them are...
865
Authors: Wu Zhao, De Jie Chen
Abstract:Fatigue failure is the most common failure mode of boring bar in the deep-hole boring processing system. For solving the problem of fatigue...
2264