Effect of Creep Holding Time on the Fatigue Behavior in P92 Steel Weldment at High Temperature
  Abstract

In this study, the crack growth behavior in P92 steel (9%Cr-2%W) weldment was investigated at 600ı under the load of trapezoidal wave shape with various holding times. The relationship between the crack growth behavior and holding time was studied and it was characterized using the ΔK and (Ct)avg parameters. The number of micro-voids/cavities at the crack tip and fracture modes were examined and the relationship between crack growth rate and holding time was investigated.

  Info
Periodical
Materials Science Forum (Volumes 475-479)
Main Theme
Edited by
Z.Y. Zhong, H. Saka, T.H. Kim, E.A. Holm, Y.F. Han and X.S. Xie
Pages
4211-4214
DOI
10.4028/www.scientific.net/MSF.475-479.4211
Citation
B. J. Kim, B. S. Lim, "Effect of Creep Holding Time on the Fatigue Behavior in P92 Steel Weldment at High Temperature", Materials Science Forum, Vols. 475-479, pp. 4211-4214, 2005
Online since
January 2005
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: C.S. Jeong, Byeong Soo Lim
Abstract:At high temperatures typical for service conditions in fossil power plants, the creep fracture is dominated by the formation, growth and...
1319
Authors: Byeong Soo Lim, Bum Joon Kim, D. Kim, J.W. Kim, Dong Bok Lee
Abstract:In this study, the creep-fatigue crack growth behavior was investigated at 600°C under the maximum load with various dwell times. Test...
794
Authors: C.S. Jeong, Si Yon Bae, Byeong Soo Lim
Abstract:The structures connected by welding are fractured often in Heat Affected Zone (HAZ) when cracks grow under high-temperature and high-pressure...
446
Authors: C.S. Jeong, Byeong Soo Lim
Abstract:As the operation time of a power plant increases, the degradation and the cracks inside of the structure exposed to high temperature will...
1858
Authors: Chan Seo Jeong, Si Yeon Bae, Byeong Soo Lim
Abstract:The results of cavity inspection in uniaxial creep tests and creep crack growth tests were compared to determine the cavity effect. The...
620