Effect of Warm Rolling on Microstructure and High Temperature Mechanical Behavior of a Nano-Structured Al-8Fe-2Mo-2V-1Zr Alloy
  Abstract

Mechanical properties of a nano-structured Al-8Fe-2Mo-2V-1Zr alloy produced by spray forming and subsequent hot-extrusion at 420°C were investigated in terms of tensile test as a function of temperature. Warm rolling was adapted as an additional process to expect further refinement in microstructure. Well-defined equiaxed grain structure and finely distributed dispersoids with nano-scale in particle size were observed in the spray formed and hot extruded sample (as-received sample). The average grain size and particle size were measured to 500 nm and 50 nm, respectively. While it was found that warm rolling gives rise to precipitate fine dispersoids less than 10 nm without influencing the grain size of matrix phase, in the temperature range of RT∼150°C, distinguishable changes in ultimate tensile strength were not found between the as-received and warm-rolled samples. At elevated temperatures ranging from 350 to 550°C, warm-rolled sample showed a higher value of elongation than as-received one although similar values of elongation were observed between two samples at temperatures lower than 350°C.

  Info
Periodical
Materials Science Forum (Volumes 486-487)
Edited by
Hyung Sun Kim, Sang-Yeop Park, Bo Young Hur and Soo Wohn Lee
Pages
411-414
DOI
10.4028/www.scientific.net/MSF.486-487.411
Citation
W. Y. Kim, J. S. Park, M. S. Kim, "Effect of Warm Rolling on Microstructure and High Temperature Mechanical Behavior of a Nano-Structured Al-8Fe-2Mo-2V-1Zr Alloy", Materials Science Forum, Vols. 486-487, pp. 411-414, 2005
Online since
June 2005
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Yoshimasa Takayama, Y. Otsuka, Toshiya Shibayanagi, Hajime Kato, Kunio Funami
Abstract:Grain refinement and high temperature deformation in two kinds of magnesium alloys subjected to friction stir processing (FSP) have been...
55
Authors: Juraj Lapin, Zuzana Gabalcová, Tatiana Pelachová, Oto Bajana
Abstract:Microstructure and mechanical properties of a new cast air-hardenable intermetallic Ti-46Al-8Ta (at.%) alloy are studied. Primary...
1368
Authors: Xin Tao Liu, Man Ping Liu, Qu Dong Wang, Wei Guo, Dong Di Yin
Abstract:Mg-3wt.%Y alloys were processed by cyclic extrusion and compression (CEC) up to 7 passes at different temperatures from 375 to 450 °C,...
767
Authors: Mahmood Fatemi Varzaneh, Jose María Cabrera, Abbas Zarei Hanzaki
Abstract:A new continuous severe plastic deformation (SPD) method called accumulative back extrusion (ABE) was employed to fabricate ultra-fine...
1033
Authors: Shao Feng Zeng, Kai Huai Yang, Wen Zhe Chen
Chapter 7: Transmission and Control of Fluid
Abstract:Equal channel angular pressing (ECAP) was applied to a commercial AZ61 magnesium alloy for up to 8 passes at temperatures as low as 473K....
2124