Characteristics of Recrystallization Texture Evolution in High Magnetic Field for Interstitial Free (IF) Steel Sheet
  Abstract

High magnetic field is applied with the field direction parallel to the rolling direction during annealing of a cold rolled IF steel sheet. Results of X-ray ODF analysis show that, magnetic field annealing retards the normal recrystallization texture evolution for the IF steel sheet. It is worth noting that an abnormal increase of orientation intensity at {100}<110> is found after magnetic annealing for 25min at 650°C. When the magnetic field strength is increased from 10 Tesla to 14 Tesla, the a-fiber is further strengthened, especially the {100}<110> component. Combined with EBSD analysis results, it is considered that the magnetic field does not change the mechanism of recrystallization texture evolution for the IF steel sheet in the present case.

  Info
Periodical
Materials Science Forum (Volumes 495-497)
Edited by
Paul Van Houtte and Leo Kestens
Pages
465-470
DOI
10.4028/www.scientific.net/MSF.495-497.465
Citation
C. S. He, Y. D. Zhang, X. Zhao, L. Zuo, C. Esling, "Characteristics of Recrystallization Texture Evolution in High Magnetic Field for Interstitial Free (IF) Steel Sheet ", Materials Science Forum, Vols. 495-497, pp. 465-470, 2005
Online since
September 2005
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: T. He, Y.D. Liu, Yan Wu, Q.W. Jiang, Gang Wang, Yan Dong Wang, Liang Zuo
Abstract:An experimental setup was designed to study the recrystallization kinetics of Interstitial Free (IF) steel in this work. The 80% cold rolled...
417
Authors: Yan Wu, Yan Lu, Xiang Zhao, Liang Zuo
Abstract:The effect of magnetic field on diffusion behavior of carbon in pure iron was investigated. The results showed that the magnetic field can...
67
Authors: Zhi Gang Wang, Zheng Zhi Zhao, Ai Min Zhao, Jie Yun Ye
Chapter 2: Manufacturing and Design Science
Abstract:Deep drawing dual phase steel was designed and trial-produced in the laboratory. The microstructure and recrystallization texture was studied...
1223
Authors: Jie Yun Ye, Zheng Zhi Zhao, Zhi Gang Wang, Ai Min Zhao, Jing Jing Chen
Chapter 3: Iron and Steel
Abstract:C-Mn-Cr-Mo dual phase steel was piloted in laboratory. OM, SEM, tensile tests and XRD were used to characterize the microstructures,...
670
Authors: Ho Jun Bang, Ha Guk Jeong, Jong Beom Lee
B. Eco-Materials Processing and Design, Multifunctional Materials
Abstract:Mg alloy sheets exhibit the yield strength of 280 MPa and elongation of 18 % by rolling at 423 K. Elongation of Mg alloy sheets was improved...
190