  Abstract

TRIP steels containing Mn, Si, Al, Mo, and Nb have been examined using a laboratory simulation of a continuous hot dipped galvanizing line. The evolution of microstructure has been studied as the steel passes through the various stages of CG line processing. Tensile strengths approaching 800 MPa and ductilities approaching 30% have been achieved in the 1.5Mn-0.5Si- 1.0Al-0.015Mo-0.03Nb system.

  Info
Periodical
Materials Science Forum (Volumes 500-501)
Edited by
J.M. Rodriguez-Ibabe, I. Gutiérrez, B. López and A. Iza-Mendia
Pages
27-38
DOI
10.4028/www.scientific.net/MSF.500-501.27
Citation
A. J. DeArdo, J.E. Garcia, M. J. Hua, C. I. Garcia, "A New Frontier in Microalloying: Advanced High Strength, Coated Sheet Steels", Materials Science Forum, Vols. 500-501, pp. 27-38, 2005
Online since
November 2005
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Klaus Hulka
Abstract:In the recent years several new high strength steel grades have been developed, which exhibit improved cold formability and thus are...
91
Authors: Guo Bin Li, Zheng Zhi Zhao, Di Tang
Abstract:The microstructure evolution of 780 MPa hot dip galvanized dual-phase (DP) steel at heating stages of the annealing process was analyzed...
1331
Authors: Sourav Das, Saurabh Kundu, Arunansu Haldar
Chapter 6: Materials
Abstract:Bainitic steels, which are transformed at very low temperatures, offer an excellent combination of strength and ductility where the strength...
939
Authors: Li Hui Wang, Di Tang, Hai Tao Jiang, Ji Bin Liu, Yu Chen
Chapter 3: Steel and Iron Technology
Abstract:Effects of continuous annealing process on microstructure and properties of Si based cold-rolled TRIP Steel were studied. The results show...
472
Authors: Zhuang Li, Di Wu, Wei Lv, Shao Pu Kang, Zhen Zheng
Chapter 1: Materials Engineering. Technologies and Processing
Abstract:In this paper, ultra-high strength dual phase steel was investigated. Thermomechanical processing was conducted by using a laboratory hot...
666