Powder Characteristics and Sintering Behavior of SiO2 Coated BaTiO3
  Abstract

The Powder characteristics and sintering behavior of SiO2 coated BaTiO3 were studied. BaTiO3 powders were synthesized by the liquid mix method developed by Pechini, and silica coating was prepared by alkoxide hydrolysis method with TEOS and ethanol. The particle size of the BaTiO3 powders was ~35 nm and the thickness of the SiO2 coating layer was ~5 nm. As the SiO2 content increased, the SiO2 layers improved the powder dispersion by increasing electrostatic repulsion between the BaTiO3 particles. The Zeta potential of SiO2 coated BaTiO3 was getting close to that of pure silica with a more negative charge, compared with that of the uncoated BaTiO3. The onset temperature of shrinkage curves shifted to higher temperatures with increasing SiO2 contents.

  Info
Periodical
Materials Science Forum (Volumes 534-536)
Edited by
Duk Yong Yoon, Suk-Joong L. Kang, Kwang Yong Eun and Yong-Seog Kim
Pages
1065-1068
DOI
10.4028/www.scientific.net/MSF.534-536.1065
Citation
J. S. Park, Y. H. Han, "Powder Characteristics and Sintering Behavior of SiO2 Coated BaTiO3", Materials Science Forum, Vols. 534-536, pp. 1065-1068, 2007
Online since
January 2007
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: J. Briančin, Ľubomír Medvecký, Helena Bruncková, M. Kmecová
Abstract:[Pb(Zr,Ti)(OAc)x(OR)y] acetate-alkoxide precursor was prepared by chelating from organic Pb, Zr and Ti alkoxides by their dissolution in...
353
Authors: Nicolas Louet, Thierry Epicier, Gilbert Fantozzi
Abstract:The target of this work is to investigate the effect of small additions of SiO2 or CaO on the sintering behavior and the microstructure of...
1
Authors: Jiu Jun Xu, Ying Chun Shan, Jiang Tao Li, Qin Ji Song
Abstract:Multi-step hot pressing sintering was adopted to prepare Y-SiAlON (Y0.4Si9.6Al2.4O1.2N14.8) at 1950°C for 60 min under 25 Mpa in nitrogen...
908
Authors: Jian Feng Tong, Da Ming Cheng, Bao Wei Li, Huang Hao Ling, Wang Ling
Abstract:The influence of Lu2O3 on phase transformation and seeds morphology was investigated. The result showed that the β-Si3N4 seeds with up to 95%...
37
Authors: Adriana Scoton Antonio Chinelatto, Milena Kowalczuk Manosso, Elíria Maria Jesus Agnollon Pallone, Ana Maria Souza, Adilson Luiz Chinelatto
Abstract:Sintering in two-steps has been applied with success for densification of nanometric and submicrometer ceramic powders without grain growth....
221