The Effect of Aging on Synthesis of Zeolite at High Temperature
  Abstract

Zeolite are used as adsorbent, catalyst and ionexchang material. But it limited to extend the usage of the zeolite since almost zeolite synthesized by hydrothermal method. The purpose of this study was to synthesis zeolite by calcination at high temperature due to extend the application of zeolite, as ceramics process. The effect of aging temperature and time, crystallization temperature on the synthesis of zeolite has been studied. Aging was performed at room temperature~70°C during 0~3days. After aging, zeolite precursor sinter for 1 hours at 300, 400, 500°C in furnace. The resulting materials were characterized by XRD, TG, SEM When the aging time is less than 1 day zeolite was not synthesized. But zeolite A obtained from precursor of aging time is more than 1 day at all firing temperature. As a result the aging time and aging temperature is increased, the zeolite synthesis time is decreased. Therefore aging is benefit process on synthesis of zeolite at high temperature.

  Info
Periodical
Materials Science Forum (Volumes 620-622)
Edited by
Hyungsun Kim, JienFeng Yang, Tohru Sekino and Soo Wohn Lee
Pages
225-228
DOI
10.4028/www.scientific.net/MSF.620-622.225
Citation
Y. S. Yoo, H. J. Ban, K. H. Cheon, J. I. Lee, "The Effect of Aging on Synthesis of Zeolite at High Temperature", Materials Science Forum, Vols. 620-622, pp. 225-228, 2009
Online since
April 2009
Keywords
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Y.K. Chung, Jong Jin Park, Cheol Hong Joo, Ik Min Park
Abstract:X20CrMoV12 1 steels were exposed at three different high temperatures and various durations. Aging parameter, LMP s, was used to...
537
Authors: Sabine Begand, Thomas Oberbach, Wilfried Glien, J. Schneider
Abstract:Alumina and zirconia ceramics have been successfully used as materials for joint endoprostheses. The present study has been aimed at...
763
Authors: Bin Gou, Ji Ho Gu, Je Hyun Lee, Kwang Jun Euh, Seung Zeon Han
Abstract:The micro-hardness and electric conductivity was studied in as cast alloy Cu-Fe-P alloys which were solution treated at 980°C and aging...
267
Authors: Prachya Peasura, Bovornchok Poopat
Abstract:The Inconel X-750 indicates good hot corrosion resistance, high stability and strength at high temperatures and for this reason the alloy is...
108
Authors: Ge Chen, Jia Lu Li
Chapter 6: Measurement Technology and Instrument
Abstract:Accelerated thermal-oxidative aging tests on Nylon 66 automotive airbag material are designed and performed in this paper. After the...