Synthesis, Characterization and Electrical Properties of Single Phase La0.9Sr0.1Ga0.8Mg0.2O3
  Abstract

Single phase La0.9Sr0.1Ga0.8Mg0.2O3-δ (LSGM9182) was synthesized by a polymeric precursor route. The XRD pattern after calcination at 1300 °C for 6h indicates the formation of the perovskite without the presence of secondary phases. XRD, FTIR and TG-DTG measurements were used to examine the powder precursor as well as the intermediate and final products. SEM images indicated the small grain size of the final product. The conductivity of the sintered sample was examined by means of a.c. impedance spectroscopy and was found to be 9.10-2 S/cm at 800 °C similar to the typical value of LSGM materials.

  Info
Periodical
Materials Science Forum (Volumes 636-637)
Edited by
Luís Guerra ROSA and Fernanda MARGARIDO
Pages
874-879
DOI
10.4028/www.scientific.net/MSF.636-637.874
Citation
A. Gaki, G. Kakali, R.J. Wiglusz, W. Strek, G. Paściak, "Synthesis, Characterization and Electrical Properties of Single Phase La0.9Sr0.1Ga0.8Mg0.2O3", Materials Science Forum, Vols. 636-637, pp. 874-879, 2010
Online since
January 2010
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Gianfranco Dell'Agli, Giuseppe Mascolo, Maria Cristina Mascolo, Concetta Pagliuca, Paolo Perna, Umberto Scotti Di Uccio
Abstract:Mechanical mixtures of zirconia xerogel with variable content of crystalline Y2O3 up to 25 mol%, were hydrothermally treated by microwave...
391
Authors: Xiao Ya Li, Yun Yu, Dong Li Wang, Li Dong Chen
Abstract:[Ca2(Co0.65Cu0.35)2O4]0.624CoO2 polycrystalline samples were prepared using sol-gel method followed by spark plasma sintering....
805
Authors: Min Zhou, Jing Feng Li, Jing Liu
Abstract:The Bi2Te3 compound was synthesized by mechanical alloying (MA) of highly pure constituents of Bi and Te powders, and then was consolidated...
538
Authors: Ming Zhou, Yan Wen Tian
Abstract:This experiment composes irreversible cells using ultrafine electrolyte materials and platinum slices, to measure the ionic conductivity the...
799
Authors: Monica Sindhu, N. Ahlawat, Sujata Sanghi, Ashish Agarwal, A. Ashima, Rekha Kumari, Navneet N. Ahlawat
Chapter 4: Electronic Materials
Abstract:Potassium Sodium Niobate, Na0.5K0.5NbO3 is a promising base material for lead free piezoceramics. The polycrystalline sample Na0.5K0.5NbO3...
210