Preperties of Linear Polyaspartic Polyurea Coated Concrete under NaCl Solution Immersion and Co-Action of Load and NaCl Solution Immersion
  Abstract

In this paper both the NaCl immersion and the co-action of load and NaCl solution immersion were employed to analyze the wet adhesive property and resistance of chlorion diffusivity of two types of linear polyaspartic ester (PAE) polyureas coated concrete: B2(PAE-b-H12MDI prepolymerH66)coated concrete and F2(PAE-f-H12MDI prepolymerH62) coated concrete. The research on the adhesion of B2 and F2 coated concrete showed that the adhesion were about 2N/mm and 1.5N/mm respectively before exposure, and the adhesion reduced about 6.8% and 11.8% respectively after 10% NaCl immersion for 300 days and made 8% and 5% further decrease under the co-action of load and NaCl solution immersion, double-factor exposure for 300 days. Compared with single NaCl solution immersion, the co-action of load and NaCl solution immersion also had more influence on the chlorion diffusivity of the coated concrete. The average chlorion content of B2 and F2 coated concrete increased about 19-21%, and the diffusion coefficient of chlorion of B2 and F2 coated concrete was 10-13-10-14m2/s, due to the micro-crack of concrete in tensile area increased under bending load, accelerating chlorion diffusion and permeation. The research showed that chlorion diffusion behaviour of B2 and F2 coated concrete under the NaCl immersion and the co-action of load and NaCl solution immersion satisfied second Fick’s law.

  Info
Periodical
Edited by
Yafang Han, Tianmin Wang and Shaoxiong Zhou
Pages
28-32
DOI
10.4028/www.scientific.net/MSF.650.28
Citation
P. Lu, W. B. Huang, H. Shi, L. Zhu, "Preperties of Linear Polyaspartic Polyurea Coated Concrete under NaCl Solution Immersion and Co-Action of Load and NaCl Solution Immersion ", Materials Science Forum, Vol. 650, pp. 28-32, 2010
Online since
May 2010
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: In Seok Yoon
Abstract:The surface treatment system is one of the best options to extend the service life of marine concrete in terms of cost effectiveness versus...
765
Authors: Shi Ping Zhang, Lan Zong, Jia Ping Liu
Abstract:A detailed observation on the penetration profile of chloride ions through a crack in concrete structures was carried out. Cracks were...
113
Authors: Zheng Mao Ye, Lian Cong Zheng, Li Hua Wan, Xin Cheng
Chapter 8: Constructional Materials
Abstract:The standard diffusion calculating model is one of the models widely used to predict the concrete construction life in chloride environment....
1038
Authors: Fu Xiang Jiang, Yu Tian Wang, Tie Jun Zhao, Liang Liang Liu
Chapter 1: Materials Design
Abstract:The mechanism of concrete durability under uniaxial compressive load has been studied through chloride penetration experiments in this...
120
Authors: Hai Cheng Yang, Zhao Zhong Wang, Jian Bo Xiong
Chapter 4: Novel Constructional Materials and Functional Materials, Analysis and Technology
Abstract:Effect of concrete surface hydropobation treatment against chloride penetration have been studied by in-site exposure test. The results show...
524