Preparation of High Wear-Resistant Ceramic Parts
  Abstract

Preparation of high wear-resistant ceramic parts was studied in this paper. The mechanical property was measured by the three-point bending tester, and the microstructures were analyzed with the scanning electronic microscope (SEM). The experimental results showed that vitrified bond CM2 was suitable for the preparation of high wear-resistant ceramic parts because of its lower refractoriness, and higher bonding strength sintering at 850oC. Moreover, containing 8- 12μm CBN abrasive grains, the ceramic parts reached higher strength and higher wear resistance than other samples.

  Info
Periodical
Materials Science Forum (Volumes 675-677)
Edited by
Yi Tan and Dongying Ju
Pages
163-166
DOI
10.4028/www.scientific.net/MSF.675-677.163
Citation
A. J. Zhang, Z. C. Li, Z. H. Li, Y. M. Zhu, "Preparation of High Wear-Resistant Ceramic Parts", Materials Science Forum, Vols. 675-677, pp. 163-166, 2011
Online since
February 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Zhi Hong Li, Y.M. Zhu, Xia Wan Wu, Q.M. Yuan, Zheng Fang Yang
33
Authors: Zi Cheng Li, Ai Ju Zhang, Zhi Hong Li, Yu Mei Zhu
Abstract:Cubic boron nitride (cBN) grains treated with hydrochloric acid, nitric acid and sulphuric acid were investigated, respectively. The results...
167
Authors: Wen Rui Duan, Zi Li Kou, Li Min Wei, Xing Hui Yang, Chun Xia Li, Hong Yang Chen
Chapter 6: Polymers, Composites and Compounds
Abstract:PcBN–Al composites(PAC)have been synthesized by pressure infiltration(PI) and a general mixing method(GM)[1-3] with a wide grain sizes range...
664