Preparation and Characterization of MWCNTs/FSiPUA Hybrid Film
  Abstract

CNTs/polymer hybrid films have been studied for hydrophobic surface in recent years. In this paper MWCNTs/FSiPUA hybrid films based on the excellent hydrophobicity have been prepared for the long term objective to prevent the marine fouling. MWCNTs/FSiPUA hybrid emulsion was prepared respectively by the methods of solution mixing with ultrasonic excitation and in-situ emulsion polymerization. Chemical and physical properties of the films were investigated by FTIR, contact angle meter and water absorption. The results showed that lauryl sodium sulfate(SDS)was a better dispersant than BYK-154 prepared via solution mixing with ultrasonic excitation. The performance of hybrid films approached by solution mixing with ultrasonic excitation was better than that by in-situ emulsion polymerization when same amount of MWCNTs was filled. The study indicated that the film surface properties reached best by both technologies when the content of MWCNTs was equal to 0.15wt%.

  Info
Periodical
Edited by
Rongming Wang, Ying Wu and Xiaofeng Wu
Pages
233-237
DOI
10.4028/www.scientific.net/MSF.688.233
Citation
M. Miao, Y. H. Qi, Z. P. Zhang, Z. Zhang, "Preparation and Characterization of MWCNTs/FSiPUA Hybrid Film", Materials Science Forum, Vol. 688, pp. 233-237, 2011
Online since
June 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Chao Liu, Yu Bin Fu, Ji Yong Zheng
Abstract:Water based resins have an important application in environmental benign coating to reduce the volatile organic compounds (VOC). This work...
537
Authors: Xiao Hui Gao, Yu Feng Li, Zhou Mao Yu
Materials Engineering
Abstract:Versatate-fluorocarbon emulsion with core-shell structure was synthesized by seeded emulsion polymerization using versatate, organic fluorine...
2055
Authors: Li Ming Zhang, Xiu Lan Xin, Wei Jiang
Chapter 1: Environment Friendly Ink and Material Technology
Abstract:The water-based pigment ink jet emulsion whose particle size was less than 100nm was synthesized by the polymerization of methyl...
81
Authors: Liang Fei
Chapter 9: New Functional Materials
Abstract:Acrylate modified waterborne polyurethane (PUA) emulsion was prepared by means of core-shell polymerization processes. The structures and...
1386