Recrystallization Kinetics and Texture Evolution during Annealing of Fe-23.2Mn-0.57C Alloy
  Abstract

The recrystallization behavior of a 50% cold rolled Fe-23.2Mn-0.57C alloy was investigated during annealing at temperatures between 560°C and 670°C. The recrystallization kinetics were characterized by microhardness tests. X-ray diffractions and EBSD measurements were used to characterize the grain microstructure and texture evolution during annealing. The obtained experimental data were evaluated in terms of the JMAK model. The annealing texture in the investigated temperature range was very weak.

  Info
Periodical
Materials Science Forum (Volumes 702-703)
Chapter
Chapter 3: Deformation and Annealing
Edited by
Asim Tewari, Satyam Suwas, Dinesh Srivastava, Indradev Samajdar and Arunansu Haldar
Pages
443-448
DOI
10.4028/www.scientific.net/MSF.702-703.443
Citation
Y. P. Lu, D. A. Molodov, G. Gottstein, "Recrystallization Kinetics and Texture Evolution during Annealing of Fe-23.2Mn-0.57C Alloy", Materials Science Forum, Vols. 702-703, pp. 443-448, 2012
Online since
December 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Chang Liang Li, Hua Ding, Yong Qing Zhao, Lian Zhou
Abstract:Superplastic forming provides a good way for Ti alloys which are usually difficult to be deformed. Ti75 alloy with a nominal composition of...
2969
Authors: Zhi Guo Chen, Zi Qiao Zheng, Dong Feng Han
Abstract:The hot deformation behaviors and microstructure in Al-Cu-Li alloy containing small amount of Ag and Mg were investigated by transmission...
1925
Authors: Zhi Min Zhang, Qiang Wang, B.C. Li, X. Zhang
Abstract:Warm compression tests of AZ31 Mg alloy were carried out at five temperatures in 30°C intervals from 210°C to 330°C. The samples of...
1813
Authors: Ivo Stloukal, Jiří Čermák
Abstract:Coefficient of 65Zn heterodiffusion in Mg17Al12 intermetallic and in eutectic alloy Mg - 33.4 wt. % Al was measured in the temperature...
189
Authors: M. Kolář, Vladivoj Očenášek, J. Uhlíř, Ivana Stulíková, Bohumil Smola, Martin Vlach, V. Neubert, K. Šperlink
Abstract:The influence of plastic deformation and heat-treatment on the precipitation of Al3(Sc, Zr) particles and the effect of these precipitates...
357