Texture Evolution during Cold Rolling and Annealing in Dual Phase Steels
  Abstract

This paper investigates the bulk texture evolution during cold rolling and annealing of Dual Phase steels for different processing conditions, i.e. cold reduction within the reduction range of 45 to 73% and annealing at temperatures between 650 and 850°C, which includes the recovery, recrystallisation and partial phase transformation domains. Textures have been measured by X-ray diffraction. The results reveal that the rolling texture is strengthened during the recovery process or initial stage of recrystallisation while during recrystallisation a weak RD-ND type of texture appears. During subsequent phase transformation the RD-ND type of texture further weakens and later randomises as the second phase fraction increases beyond 75%.

  Info
Periodical
Materials Science Forum (Volumes 702-703)
Chapter
Chapter 6: Materials
Edited by
Asim Tewari, Satyam Suwas, Dinesh Srivastava, Indradev Samajdar and Arunansu Haldar
Pages
778-781
DOI
10.4028/www.scientific.net/MSF.702-703.778
Citation
J. Gautam, A. G. Miroux, J. Moerman, C. Barbatti, L. Kestens, "Texture Evolution during Cold Rolling and Annealing in Dual Phase Steels", Materials Science Forum, Vols. 702-703, pp. 778-781, 2012
Online since
December 2011
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Saidmurod Akramov, Min Gu Lee, In Soo Kim, Dong Young Sung, Byung Hyun Park, Ingi Kim
Abstract:By severe plastic deformation of metals, an ultra fine grain size can be obtained. In the present study an AA 1050 Aluminium alloy has been...
803
Authors: T. He, Y.D. Liu, Yan Wu, Q.W. Jiang, Gang Wang, Yan Dong Wang, Liang Zuo
Abstract:An experimental setup was designed to study the recrystallization kinetics of Interstitial Free (IF) steel in this work. The 80% cold rolled...
417
Authors: Zhi Gang Wang, Zheng Zhi Zhao, Ai Min Zhao, Jie Yun Ye
Chapter 2: Manufacturing and Design Science
Abstract:Deep drawing dual phase steel was designed and trial-produced in the laboratory. The microstructure and recrystallization texture was studied...
1223
Authors: Jie Yun Ye, Zheng Zhi Zhao, Zhi Gang Wang, Ai Min Zhao, Jing Jing Chen
Chapter 3: Iron and Steel
Abstract:C-Mn-Cr-Mo dual phase steel was piloted in laboratory. OM, SEM, tensile tests and XRD were used to characterize the microstructures,...
670
Authors: Ho Jun Bang, Ha Guk Jeong, Jong Beom Lee
B. Eco-Materials Processing and Design, Multifunctional Materials
Abstract:Mg alloy sheets exhibit the yield strength of 280 MPa and elongation of 18 % by rolling at 423 K. Elongation of Mg alloy sheets was improved...
190