Modification of V2O5-WO3/TiO2 Catalysts Supported on SiC Filter for NO Reduction at Low Temperature
  Abstract

The catalytic filter, a ceramic filter supported SCR catalyst, is a promising material for treating particulates and NOX simultaneously. Recently, it is found that a SiC filter supported V2O5- WO3-TiO2 [commercial catalyst system] shows a reasonable SCR activity around 320 °C [1]. In order to improve its catalytic activity at low temperatures, the effects of Pt and MnOX addition on the catalytic filter are investigated. The macro-porous TiO2 film was firstly coated on the pore surface of SiC filter element using the solution composed of the preformed TiO2 particles (P25). Catalytic filters were prepared by the impregnation of TiO2 coated-SiC filter in the solution containing the catalyst components. The MnOX-added catalytic filter showed very wide temperature window from 150-340 °C, providing NX slip concentration less than 20 ppm for the treatment of 700 ppm NO at a face velocity of 2 cm/s. Pt added-catalytic filter shifted the optimum working temperature towards the lower temperatures (180-240 °C) compared to the one without Pt (280-330 °C). It is understood that MnOX in the catalyst system roles as the main catalyst component while Pt rose as a electron modification additive.

  Info
Periodical
Solid State Phenomena (Volumes 124-126)
Edited by
Byung Tae Ahn, Hyeongtag Jeon, Bo Young Hur, Kibae Kim and Jong Wan Park
Pages
1713-1716
DOI
10.4028/www.scientific.net/SSP.124-126.1713
Citation
Y. G. Kim, J. H. Choi, L. Yu, Y. C. Bak, "Modification of V2O5-WO3/TiO2 Catalysts Supported on SiC Filter for NO Reduction at Low Temperature", Solid State Phenomena, Vols. 124-126, pp. 1713-1716, 2007
Online since
June 2007
Export
Price
$32.00
Share

In order to see related information, you need to Login.

In order to see related information, you need to Login.

Authors: Dong Lei Zou, Zha Gen Lu, Zhen Yin Sui, Hao Chen Zou, Wei Qun Sui
Abstract:The catalytic ozonation which treated nitrobenzene in extracted groundwater with high concentration was studied.The experiment showed that...
280
Authors: Feng Hua Bai, Yin Xia Zhang, Hai Quan Su, Xue Fen Li, Hui Pan, Xu Zhuang Yang
Abstract:The effect of precursors of Co/γ-Al2O3 catalysts prepared from Co(NO3)2 and...
684
Authors: Takeshi Miki, Yutaka Tai
Abstract:Fe2O3/Al2O3 catalyst was prepared and the catalytic oxidation of toluene over the catalyst was...
101
Authors: Yan Gao, Tao Luan, Tao Lv, Hong Ming Xu
Chapter 1: Environment Materials and Chemical Environment
Abstract:The SCR catalysts were produced with V2O5, WO3, MoO3 and anatase type TiO2. The thermo stability of the catalyst with different MoO3 loading...
58
Authors: Jun Feng Wen, Xia Liu
Chapter 11: Energy Chemical Engineering and Processes
Abstract:Active carbon (AC) supported Ni–Cu bimetallic catalysts for the direct synthesis of acetic acid (AcOH) from CH3OH and CO were...
1383