Papers by Author: A. Kasuya

Abstract: The details of energy relaxation and multiple phonon scattering of a resonantly excited electron-hole pair confined in CdSe nanoparticle are studied at low temperature. Simple variational calculation of Ritz type have been performed to explain relaxation of excitons resonantly excited in CdSe nanoparticles in the case if initial photon absorption and creation of electron-hole pair takes place in the peripheral part of nanoparticle.

Abstract: Silica-coating of AgI nanoparticles with a Stöber method was carried out to find out reaction conditions for control of the shell thickness. The AgI nanoparticles were prepared from AgClO4 and KI with the use of 3-mercaptopropyltrimethoxysilane (MPS) as a silane coupling agent and dimethylamine (DMA) catalyst for alkoxide hydrolysis. The silica-coating was performed at 4.5×10-6-4.5×10-5 M MPS, 11-20 M water, 0.002-0.1 M DMA and 0.005-0.04 M tetraethylorthosilicate at AgI concentrations of 0.1-1 mM. Consequently, AgI-silica core-shell particles could be prepared with the use of 4.5×10-5 M MPS, 20 M water, 0.01 M DMA and 1 mM AgI. Silica shell thickness could be varied from 15 to 28 nm with an increase in the TEOS concentration from 0.005 to 0.04 M.