Papers by Author: Bin Deng

Abstract: Objective: To compare the effectiveness of different proportional nHA / PLA application in alveolar bone preservation. Methods: After extraction, apply extraction socket filling based on the alveolar bone defect model due to absorption in Beagle dog. Implant materials are divided into 3 different groups: nHA / PLAI, nHA / PLAII and the control group. Samples of the alveolar bone were collected at Week 4 and 8, respectively for the bone resorption assessment, bone density measurement, and histological examination. Results: After nHA / PLA implantation, the alveolar bone preservation was significantly improved. There was no difference in the alveolar bone preservation between the nHA / PLAI and nHA / PLAII groups. However, the sample which are 8w from group I, have higher bone density and have complete absorption in their dental material nest .Therefore group I is better than group II. Conclusions: The results can provide a reliable basis for the application of alveolar bone preservation in basic research and selection of clinical materials.

Abstract: Objective: To evaluate the colouration of zirconia ceramic by adding two kinds of rare earth oxides. Methods: Added different concentrations of Fe₂O₃ and CeO₂ in tetragonal zirconia poly crystals stabilized with 3Y-TZP powder compacted at 200MPa using cold isostatic pressure, and fully sinter. The chromaticity of sintered bodies was measured with spectrophotometer. Results: self-colored zirconia by two kinds of rare earth oxides: The lightness of zirconia by adding cerium oxides was about 85 and a* decreased slightly. The color shifted to more yellow-green color. The chroma of the ceramics became more intensity, the lightness decreased with the increasing of the content of ferrum oxides and the color change to red-yellow direction. Conclusion: Zirconia ceramic could be colorized by Fe₂O₃ and CeO₂.

Abstract: Objective: We aimed to develop a multi-functional CCS/CCM (Computerized Color Selecting/Computer Color Matching) software so as to provide more practical colorimetric software for clinical use and further researches. Methods: This software used the 6 dental prosthetic materials and color data from 4 shade guide system which were most frequently-used in clinic currently as basic database, to program 5 functional blocks including respectively CCS/CCM system; Dental Material Chromatic Value System; Vita Information System; Transformation of Colorimeter System; and Chromatic Value Difference Analysis. These modules had the functions of information inquiry of different types of dental materials and their corresponding chromatic value, color matching, transforming, and color difference analysis. Results: The software had a convenient operation interface which could guarantee a stable performance. Containing various shade block and chromatic value, and transformation among different colors, this software analysed the color difference in the database, improved the accuracy and reliability of dental color choosing, and, to some extent, increased the color repetition rate of prosthesis. Conclusion: The software could well meet the needs of clinical dental colorimeter and choosing, increase the color repetition rate of prosthesis, and easily finish the transformation among different colors. It had more functions to adapt clinical need.

Abstract: The need for bone repair has increased as the population ages. However, currently, the bone grafts still have some disadvantages, such as low compressive strength and porosity, which limit their use. In order to solve these disadvantages, in this study, the porous beta-tricalcium phosphate (β-TCP) anorganic bone graft were prepared from healthy bovine cancellous bone by cell-free, defat and twice calcinations. X-ray diffraction (XRD) was used to investigate the chemical composition of the bone graft. And the morphology, porosity and mechanical strength of the bone graft were also evaluated. The results showed that most constituent of the bone graft was β-TCP. In addition, the bone graft scaffold exhibited the macro and micro porous structure and the porosity was 57.63%, just as the nature cancellous bone. The compressive strength was 4.47±0.63MPa. Above all, the porous β-TCP anorganic bone graft not only has similar chemical composites as the nature cancellous bone, but also it can effectively retain the porous structure of natural cancellous bone and provides optimal channels for the ingrowth of new bone and blood vessels.Therefore, the porous β-TCP anorganic bone graft is a potential biomaterial in bone tissue engineering.

Abstract: The aim of this invitro study was to evaluate the fracture resistance of endodontically treated canines restored with one-piece milled zirconia post and core in the varying ferrule modes. Fifty recently extracted human maxillary canines were endodontically treated and randomly divided into 5 groups of 10 specimens each. According to the defect degree of ferrule, intact ferrule was classified as group A and served as control, 2 mm ferrule height without buccal ferrule was classified as group B, 2 mm ferrule height without mesial and buccal ferrule was classified as group C, 2 mm ferrule height without mesial, buccal and lingual ferrule was classified as group D, no ferrule preparation was classified as group E. All of the teeth were restored with one-piece milled zirconia post and core, and zirconia crowns. The teeth were prepared to standardized specifications. The restored teeth were loaded to fracture at a 135° angle to their long axis, at a cross-head speed 0.5 mm/min, and the load (N) at failure was recorded. Statistical analysis was performed by SNK pairwise multiple comparisons (α=0.05). The mean fracture resistance of five groups as follows: 1019.30±139.01N for group A, 861.20±105.67N for group B, 833.70±100.56N for group C, 733.20±96.91N for group D, 698.00±99.90N for group E. The fracture resistance of restored teeth between group B and group C, group D and group E had no statistically significant difference(P>0.05). The fracture resistance of the rest pairwise group comparisons had statistically significant difference(P<0.05). Increasing the absence degree of ferrule, it was found that the fracture resistance decrease. The buccal and lingual ferrule were more important than mesial ferrule for enhanced fracture resistance. This in vitro study supports evidence that reserving the buccal and lingual ferrule is a key point to increase the fracture resistance of canines restored with one-piece milled zirconia post and core.

Abstract: To assess the color stability of different resin cements after accelerated ageing. Four different resin cements were included in the study (1mm thickness). The resin cements were bonded to ceramic disks (0.5mm thickness) built with the VITABLOCS MARK-Ⅱ ceramic (n=7). All of the samples were stored in 37°C distilled water at dark. Then color measurement were determined using spectrophotometric before and after accelerated ageing in a weathering machine with a total energy of 150kJ/m². Changes in color (ΔE) were obtained using the CIE Lab system coordinates where a ΔE data above 3 was accepted as visible discoloration. The ΔE of Superbond C&B, RelyX ARC, Variolink Veneer and Tetric Flow were 2.24±0.52, 2.47±0.28, 0.62±0.31 and 0.72±0.31 respectively. The Superbond C&B and RelyX ARC achieved significant higher ΔE than the other groups (P0.05). All of the resin cements assessed in this study show varying degrees of discoloration after accelerated ageing. However, the color change are not beyond the clinical aesthetic demand. And the Tetric Flow and Variolink Veneer demonstrate a higher color stability.

Abstract: Aim To explore pigmented glass for infiltration and investigate its physical and mechanical properties. Methods The pigmented glass was prepared by melting glass components in an alumina crucible at 1400°C for 2h. The thermal properties were tested using a Setaram-TGDTA 92 analyzer; three point bending strength and fracture toughness were also tested; the microstructure of the glass was studied using a scanning electron microscope. Results The thermal expansion coefficient over the range 20–600 °C was 6.2 × 10-6 °C -1, Tg was about 690 °C, the density, bending strength, fracture toughness and Vickers hardness were 2.23 g/cm3, 118 MPa, 1.22 MPam1/2, and 7.4 GPa respectively. Conclusion The pigments have no detrimental effects on the physical and mechanical properties; thus the pigmented glass for infiltration has favorable physical and mechanical properties and also good compatibility with presintered porous alumina.

Abstract: The purpose of this study was to study effects of the mechanical properties of veneering porcelain on stress distribution of dental zirconia layered structure by three-dimensional finite element analysis. A 3-D geometric model of the first maxillary molar was established, a tooth preparation was simulated by the Imageware software. A crown was designed and divided into three layers: core, middle layer and outer veneer layer. The elasticity modulus of the middle layer was 70GPa for the control model up to 175GPa for the tested models. Loads of 200N were applied over a 1 mm diameter area beneath the tip of the mesial-distal cusp, simulating typical occlusal contact areas, the stress distribution of the crown systems were analyzed. Results show that within the geometry of the crown configuration, one concentration district of maximum principal stress occurred on the occlusal surface closely proximal to the loading position, several sub-maximum principal stress area were observed, such as margin regions of the mesial face, lingual face, distal faces, buccal face and occlusal fossa. Middle layer with higher modulus can effectively disperse the stress concentration in the layered zirconia all-ceramic crown system.

Abstract: To evaluate the masking ability of IPS e.max all-ceramics system of HO series. IPS e.max Press HO ingots were fabricated into twenty cylindrical specimens (n=5) with the diameter of 13mm and four different thinknesses (0.4mm, 0.6mm, 0.8mm, 1.0mm). All specimens after veneered, gazed and cemented to metal substrate disks (thickness 3mm, diameter 13mm) were measured on both the white background and metal substrate disks background using a spectrophotometer and values of L, a and b were calculated to compare color differences among four groups. Meanwhile ΔE with the preselected required color (A2 color) were calculated. ΔE<1.5 was considered a clinically acceptable color match. In the 0.4mm thickness specimens group, the values of L, a and b significantly increased (-1.36±0.05, -0.15±0.06, -1.46±0.02, respectively) between the white background and abutment background. But there were no significant color differences in the other three groups (P<0.05). In the 0.6mm and 0.8mm thicknesses specimens groups, the color difference values (0.71±0.04, 1.14±0.06, respectively) with A2 color were less than the defined value. Thus the cylindrical specimens with the thickness of 0.6mm, 0.8mm and 1.0mm could mask the metal substrate disks background sufficiently and the thickness of 0.6mm and 0.8mm had an acceptable color match compared with the target color. IPS e.max all-ceramics system of HO series can produce clinically acceptable color match and have the capacity to mask a dark background such as a dark tooth or core buildup material.

Abstract: Despite the expanded application for zirconia in restoration dentistry, there is less clear recommendation in the literature regarding the relation between zirconia surface roughness and its shear bond strength to resin cements. The aim of this study was to assess the effect of surface roughness of Cercon zirconia on its shear bond strength to resin cements. 66 Zirconia rectangular specimens (10 mm×10 mm×3 mm) were prepared from Cercon zirconia blocks, finished using a diamond rotary cutting instrument, sintered, and then assigned into 6 groups. The specimens in the first group without polishing were used as control. Other groups were polished against 120#, 240#, 360#, 500# and 600# sand paper after sintered, respectively. Ceramic surface were analyzed by scanning electron microscopy (SEM) and Surface profilometer. 10 samples of each group were bonded with Variolink N resin cements respectively and submitted to shear bond strength test. Shear bond strength was measured and statistically analyzed. The results showed that the population means of 6 groups of samples were not equal. There was no significant difference between control group and 600# sand paper treated group, 500#, 360# and 240# sand paper treated groups (P>0.05), but a significant difference among the other groups (P<0.05). Findings of this study revealed that the shear bond strength might be raised by increasing the surface roughness of Cercon zirconia. Therefore, the surface roughness of Cercon zirconia has an effect on the shear bond strength, but is not the determining factor in clinical use.