Papers by Author: Bong Ho Lee

Abstract: Ultrafine TiO2 powders as rutile and anatase phase were simply precipitated at room temperature for only tens of hours by simply controlling the pH value and Ti4+ concentration via aqueous TiCl4 solution. Under the optimal pH value and Ti4+ concentration, the average particle size of powders with rutile phase was 3.7nm, while that of powders with anatase phase was 3.0nm. The average particle size was calculated from the broadening of corresponding X-ray spectral peaks by Scherrer formula. In addition, 3.0 mol.l-1 are suggested to be used as concentration of stock solutions instead of the current concentration 2.0 mol.l-1.

Abstract: After the 9∙11 terrorism and America-Iraq war, apprehension of mass destruction weapons such as bio-chemical agents calls for much more sensitive sensors which can detect toxic gases. In this study, semiconductor gas sensors based on tin oxide were examined to detect chemical agent simulants: dimethyl-methyl-phosponate (DMMP), di(propylene glycol) methyl ether (DPGME), acetonitrile, and dichloromethane. DMMP((CH3O)3), DPGME(C7H16O3), acetonitrile(CH3CN), and dichloromethane(CH2Cl2) gases are the simulants of nerve agent-sarin, vesicant agent-HN(N(CH2CH2Cl)3), blood agent-AC(HCN), and choking agent-CG(COCl2) gases, repectively. The SnO2 powder was prepared by a coprecipitation method from the mixture of tin chloride and zinc acetate dihydrate. Zinc oxide was doped into SnO2 from 1 wt% to 4 wt% to improve its reliability and sensitivity. To fabricate a thick film, powders were made into paste with organic binder of ethyl cellulose and screen-printed on the alumina substrate. The phase development and morphology of ZnO-doped SnO2 film were investigated by XRD (X-ray diffraction analysis), BET (surface and pore size analyzer), and SEM (scanning electron microscope). The gas sensing characteristics for target gases were examined with a flow-type measurement system. The concentrations of simulants were controlled from 500 ppb to 1500 ppb, and working temperatures were regulated from 250  to 400 .