Papers by Author: Carlo Gualco

Abstract: In plasma facing components (PFC) for nuclear fusion reactors tungsten or carbon based tiles need to be cooled through a heat sink. The joint between the PFC and the heat sink can be realized using a brazing process through the employment of compliant layer of either a low yield material, like copper, or a high yield material, like molybdenum. Experimental verification of the induced stresses during the brazing process is of vital importance. Strains and residual stresses have been measured in Mo/CuCrZr brazed tiles using neutron diffraction. The strains and stresses were measured in Mo tile along the weld direction and at different distances from it. The experimental results are compared with Finite Element Simulations.

Abstract: In Plasma Facing Components (PFCs) for nuclear fusion reactors, the protective material, carbon based or tungsten, has to be joined to the copper alloy heat sink for optimum heat transfer. High temperature vacuum brazing is a possible joining process as long as a proper interlayer is introduced to mitigate the residual stresses due to the mismatch of thermal expansion coefficient (CTE). Pure copper can act as plastic compliant layer, however for carbon based materials a proper structuring of the joining surface is necessary to meet the thermal fatigue lifetime requirements. In this work pure molybdenum and tungsten/copper Metal Matrix Composites (W-wires in Cu-matrix) interlayers have been studied as alternative to pure copper for carbon based protective materials in flat tile configuration. Finite element simulations of the brazing process have been performed to evaluate the expected residual stress reduction near the metal-carbon interface. In fact it has been demonstrated that stiff low CTE interlayers can shift the peak stresses from the weak carbon-metal interface to the strongest metal-metal one. Relevant samples have been manufactured and subjected to preliminary metallographic and thermal shock tests. Results obtained so far are encouraging and active cooled mock-ups are being prepared for high heat flux testing. Research work is in progress as regards monoblock configuration with both Wf/Cu MMC and graded Cu/W plasma sprayed and HIPped layers.