Abstract: The mechanical properties and microstructure of the as-extruded ZM21 magnesium alloy and its modified alloy ZME210 with addition of 0.35wt% cerium were investigated with different extrusion ratios from 14 to 182 by using mechanical property test, microscopic structure quantitative analysis, SEM observation and energy spectrum analysis. The results showed that both ZM21 and ZME210 had an extrusion ratio limit for grain refining, and the grains were found to be finer with higher extrusion ratio when the ratio was not higher than the limit value. The extrusion ratio limit for the best effect for grain refining of ZME210 is lower than that of ZM21. It was found that the Ce can refine the grains effectively after hot extrusion with different extrusion ratios. The effects of Ce on the microstructure and mechanical properties were analyzed.

Abstract: The flow stress-strain curves and other information during hot compression testing of AZ61B magnesium alloy was investigated by simulated test on Gleeble-1500D thermal-mechanical simulator. The relations between Z and other characteristic value, including peak stress, peak strain and grain size, was calculated by regression analysis. The mathematical model of flow stress was introduced to predict the flow stress. The predicting values is close to the experimental values with not more than 10% error.

Abstract: The microstructures and mechanical properties of Mg-Zn-Zr-Y alloy extruded bar with different heat treatment processes were investigated, including solution treatments of 400 oC, 450 oC and 500 oC for 3 hours followed by 170 oC×24h aging treatment, and solely aging treatments of 160 oC, 180 oC for 24hours without solution after extruding. By comparing the grain size, strength and elongation of the samples, the heat treatment processes for extruded products with high strength and with medium strength were recommended.