Papers by Author: Chuan Xin Zhai

Abstract: Using montmorillonite (MMT) and sodium carboxymethylcellulose (CMC) as raw materials, CMC/MMT nanocomposites were prepared by the solution intercalation technique. The microstructures of MMT before and after being intercalated were characterized by X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM). The results of XRD showed that when the adding amount of CMC increased from naught to 70wt%, the structures of MMT have no change basically; when the adding amount of CMC increased to 80wt%, the decrease of MMT (001) was significant; when the adding amount of CMC reached to 90wt%, the diffraction peak of (001) disappeared, which indicated that the layers of MMT have been exfoliated along (001) and the CMC/MMT intercalated structure has been obtained. The observations by HRTEM showed that the shapes of MMT are layer aggregation or agglomerated particles. The MMT added with 90wt% CMC has changed into intercalated structure with alternating MMT and CMC order mainly, and the intercalated structure was characterized at the atomic scale.

Abstract: The Fe-Based Al2O3-TiC Ceramic Composite was fabricated by combining the methods of Self-propagating High-temperature Synthesis with casting. The microstructures of ceramic layer and interface were characterized via SEM, EDS and X-ray diffraction. The Results show that the microstructure of ceramic layer is dense, and the in-situ Al2O3 and TiC particles with size of 1-2 μm are distributed on the ferrite matrix. The hardness of compact ceramic layer reaches 48HRC, and it has graded distribution from ceramic layer to the ferrite matrix. The composite interface between ceramic and matrix is compact, and takes on flexuous. The composite material bonds in a metallographic manner, with high bonding strength.